Surface characteristics and fatigue behavior of shot peened Inconel 718

[Display omitted] •Shot peening has a detrimental effect on fatigue life in low cycle fatigue.•Shot peening can increase fatigue life from two to twenty times in HCF.•The presence of significant residual stresses is the controlling factor in HCF.•Shot peening induced residual stresses mainly redistr...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	International journal of fatigue Jg. 110; S. 10 - 21
Hauptverfasser:	Klotz, T., Delbergue, D., Bocher, P., Lévesque, M., Brochu, M.
Format:	Journal Article
Sprache:	Englisch
Veröffentlicht:	Kidlington Elsevier Ltd 01.05.2018 Elsevier BV
Schlagworte:	Aerospace industry Aircraft components Compressive properties Crack initiation Crack propagation Deformation Fatigue Fatigue cracks Fatigue failure Fatigue life Fatigue tests Fracture mechanics High cycle fatigue Inconel 718 Low cycle fatigue Materials fatigue Mechanical components Nickel base alloys Residual stress Residual stresses relaxation Shot peening Strain hardening Stress relaxation Superalloys Surface chemistry Surface properties Surface roughness dσcomp=0 E El XRD RSm σu Av σmin Nf εp Residual stresses relaxation σcomp,max Crack initiation σsurf Rt dσcomp,max σy0.2 Inconel 718 Fatigue Shot peening Bal AR Rσ β σmax LB 12S2 FWHM λ ν
ISSN:	0142-1123, 1879-3452
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!