High‐Quality Cs2AgBiBr6 Double Perovskite Film for Lead‐Free Inverted Planar Heterojunction Solar Cells with 2.2 % Efficiency

All‐inorganic double‐metal perovskite materials have recently gained much attention due to their three dimensionality (3D) and non‐toxic nature to replace lead‐based perovskite materials. Among all those double perovskite materials, theoretical works have demonstrated that Cs2AgBiBr6 shows high stab...

Celý popis

Uložené v:
Podrobná bibliografia
Vydané v:Chemphyschem Ročník 19; číslo 14; s. 1696 - 1700
Hlavní autori: Gao, Weiyin, Ran, Chenxin, Xi, Jun, Jiao, Bo, Zhang, Wenwen, Wu, Mincai, Hou, Xun, Wu, Zhaoxin
Médium: Journal Article
Jazyk:English
Vydavateľské údaje: Germany Wiley Subscription Services, Inc 17.07.2018
Predmet:
anti-solvent
Cs2AgBiBr6
Energy conversion efficiency
Heterojunctions
lead-free double perovskite
micro-sized grains
Morphology
Perovskites
Photovoltaic cells
planar heterojunction solar cells
Solar cells
Stability
Cs2AgBiBr6
anti-solvent
planar heterojunction solar cell
lead-free double perovskite
micro-sized grains
ISSN:1439-4235, 1439-7641
On-line prístup:Získať plný text
Tagy: Pridať tag
Žiadne tagy, Buďte prvý, kto otaguje tento záznam!
Popis
Shrnutí:All‐inorganic double‐metal perovskite materials have recently gained much attention due to their three dimensionality (3D) and non‐toxic nature to replace lead‐based perovskite materials. Among all those double perovskite materials, theoretical works have demonstrated that Cs2AgBiBr6 shows high stability and possesses a suitable band gap for solar‐cell applications. However, the film‐forming ability of Cs2AgBiBr6 is found to be the utmost challenge hindering its development in thin‐film solar‐cell devices. In this work, a high‐quality Cs2AgBiBr6 film with ultra‐smooth morphology, micro‐sized grains, and high crystallinity is realized via anti‐solvent dropping technology and post‐annealing at high temperature. After optimization, the first example of an inverted planar heterojunction solar‐cell device based on Cs2AgBiBr6 exhibits a power conversion efficiency of 2.23 % with VOC=1.01 V, JSC=3.19 mA/cm2, and FF=69.2 %. Besides, the device shows no hysteresis and a high stability. A high‐quality double perovskite film is prepared by fast crystallization via the anti‐solvent dropping method. Micro‐sized grains and a high crystallinity of the film can be obtained by a post‐annealing process. The resulting inverted planar heterojunction solar‐cell devices show a decent efficiency of 2.23% with no hysteresis and a high stability.
Bibliografia:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:1439-4235
1439-7641
DOI:10.1002/cphc.201800346