A new zeolite formed from interlayer expansion of the precursor COK-5

The layered silicate COK-5 has been used for an interlayer expansion reaction with dichlorodimethylsilane (DCDMS) at 180 °C to interconnect neighboring layers, yielding a new and crystalline microporous framework. The samples containing the methyl functional groups in the as-made form and having OH...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Microporous and Mesoporous Materials Ročník 214; s. 204 - 209
Hlavní autoři: Bian, Chaoqun, Wu, Qinming, Zhang, Jian, Chen, Fang, Pan, Shuxiang, Wang, Liang, Meng, Xiangju, Müller, Ulrich, Feyen, Mathias, Yilmaz, Bilge, Gies, Hermann, Zhang, Weiping, Bao, Xinhe, De Vos, Dirk, Yokoi, Toshiyuki, Tatsumi, Takashi, Xiao, Feng-Shou
Médium: Journal Article
Jazyk:angličtina
Vydáno: Elsevier Inc 15.09.2015
Elsevier BV
Témata:
COK-5
DCDMS
Interlayer expansion
Lamellar precursor
Zeolite
Lamellar precursor
Interlayer expansion
COK-5
Zeolite
DCDMS
ISSN:1387-1811, 1873-3093
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:The layered silicate COK-5 has been used for an interlayer expansion reaction with dichlorodimethylsilane (DCDMS) at 180 °C to interconnect neighboring layers, yielding a new and crystalline microporous framework. The samples containing the methyl functional groups in the as-made form and having OH groups in the calcined form were designed as COE-5 and calcined COE-5. These samples were characterized with X-ray diffraction (XRD), N2 sorption isotherms, inductively coupled plasma optical emission spectrometry (ICP-OES), infrared spectroscopy (IR), high-resolution transmission electron micrograph (HRTEM), thermogravimetry-differential thermal analysis (TG-DTA), and 29Si and 13C solid-state magic-angle spinning nuclear magnetic resonance (MAS NMR), as well as the contact angle techniques. XRD patterns and HRTEM images suggest that the sample interlayer spacing has been expanded by nearly 0.5 Å. The N2 sorption isotherms of the materials show the BET surface areas are 165 m2/g for COE-5 and 340 m2/g for calcined COE-5. 29Si and 13C MAS NMR as well as IR spectroscopy confirm the insertion of the linker group -Si(CH3)2- connecting neighboring layers. Interestingly, calcined COE-5 shows enhanced catalytic performance in the acetalisation of glycerol with acetone to produce solketal, compared with COK-5. [Display omitted] •COE-5 zeolite has synthesized via an interlayer expansion of COK-5 layers.•The COE-5 interlayer spacing has been expanded to nearly 0.5 Å.•The sample wettability can be adjusted by controlling the methyl and silanol groups.•The COE-6 zeolite is very active in catalytic acetalisation of glycerol to solketal.
ISSN:1387-1811
1873-3093
DOI:10.1016/j.micromeso.2015.04.017