Controlling the stability of a Fe–Ni reforming catalyst: Structural organization of the active components

[Display omitted] •Enhanced control of the stability of carbon resistant Fe–Ni/MgAl2O4.•Formation of a core shell alloy with Fe–Ni in the core and Fe–Ni–Pd in the shell.•Catalyst with Ni:Pd molar ratio of 75:1 showed the best performance.•The addition of Pd to Fe–Ni reduces the tendency of Fe to seg...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	Applied catalysis. B, Environmental Ročník 209; s. 405 - 416
Hlavní autoři:	Theofanidis, Stavros Alexandros, Galvita, Vladimir V., Sabbe, Maarten, Poelman, Hilde, Detavernier, Christophe, Marin, Guy B.
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Amsterdam Elsevier B.V 15.07.2017 Elsevier BV
Témata:	Bimetals Carbon dioxide Catalyst stability Catalysts Control stability Deactivation Fe–Ni alloy In situ XRD Iron Methane Methane reforming Nickel Oxidation Reduction Reforming Sintering Surface layers Synthesis gas Temperature effects X-ray diffraction Catalyst stability Methane reforming Synthesis gas In situ XRD Fe–Ni alloy
ISSN:	0926-3373, 1873-3883
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!