Synergistic Effect of APP and TBC Fire-Retardants on the Physico-Mechanical Properties of Strandboard

This study explored the feasibility of fabricating fire-retardant strandboard with low mechanical properties deterioration to the physico-mechanical properties. A hybrid fire-retardant system of ammonium polyphosphate (APP) and 1,3,5-tris(2,3-dibromopropyl)-1,3,5-triazinane-2,4,6-trione (TBC) was in...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Materials Ročník 15; číslo 2; s. 435
Hlavní autoři: Tian, Feiyu, Xu, Deliang, Xu, Xinwu
Médium: Journal Article
Jazyk:angličtina
Vydáno: Switzerland MDPI AG 07.01.2022
MDPI
Témata:
Adhesives
Curing
Diphenyl methane diisocyanate
Epoxy resins
Feasibility studies
Flame retardants
Hybrid systems
Impact strength
Influence
Infrared radiation
Mechanical properties
Modulus of elasticity
Modulus of rupture
Strandboard
Stress concentration
Synergistic effect
Tensile strength
Thermal stability
Thermogravimetric analysis
Wood
United States > US
China
Germany
strandboard
ammonium polyphosphate (APP)
fire retardant
1,3,5-tris(2,3-dibromopropyl)-1,3,5-triazinane-2,4,6-trione (TBC)
ISSN:1996-1944, 1996-1944
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:This study explored the feasibility of fabricating fire-retardant strandboard with low mechanical properties deterioration to the physico-mechanical properties. A hybrid fire-retardant system of ammonium polyphosphate (APP) and 1,3,5-tris(2,3-dibromopropyl)-1,3,5-triazinane-2,4,6-trione (TBC) was investigated. Thermogravimetric analysis results show that both APP and TBC enhance the thermal stability and incombustibility of wood strands. An infrared spectrum was applied to investigate the effect of flame retardants on the curing behaviors of polymeric diphenylmethane diisocyanate (PMDI) resin. Based on the results of limiting oxygen index (LOI) and Cone calorimetry (CONE), APP and TBC both lead to a higher fire retardancy to strandboard. It is worth mentioning that the two flame retardants lead to evidently differential influences on the modulus of rupture (MOR), modulus of elasticity (MOE), internal bond (IB), and water-soaking thickness swelling (TS) properties of strandboard. Hence, a hybrid flame retardant is prominent in manufacturing strandboard with both good fire retardant and satisfying physico-mechanical properties.
Bibliografie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
content type line 23
ISSN:1996-1944
1996-1944
DOI:10.3390/ma15020435