Electrodeposition of a Ni-P-Ti3C2Tx/MoS2 coating incorporating MoS2 intercalated Ti3C2Tx particles

As a promising material, Ti3C2Tx has received much attention in recent years for brilliant performances in conductivity and lubricity. In order to modify the property of Ti3C2Tx, MoS2 intercalated Ti3C2Tx (Ti3C2Tx/MoS2) powders are made from hydrothermal reaction, which can prohibit oxidization for...

Celý popis

Podrobná bibliografie

Vydáno v:	Surface & coatings technology Ročník 354; s. 119 - 125
Hlavní autoři:	Du, Yingchao, Wang, Dongdong, Si, Pengchao, Wei, Lianqi, Wang, Yongliang, Yu, Bo, Zhang, Xiaomeng, Ye, Shufeng
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Elsevier B.V 25.11.2018
Témata:	Microhardness Ni-P-Ti3C2Tx composite coating Ni-P-Ti3C2Tx/MoS2 composite coating Ti3C2Tx/MoS2 powder Tribological property Tribological property Ni-P-Ti3C2Tx/MoS2 composite coating Ni-P-Ti3C2Tx composite coating Ti3C2Tx/MoS2 powder Microhardness