Surface characteristics and fatigue behavior of shot peened Inconel 718

[Display omitted] •Shot peening has a detrimental effect on fatigue life in low cycle fatigue.•Shot peening can increase fatigue life from two to twenty times in HCF.•The presence of significant residual stresses is the controlling factor in HCF.•Shot peening induced residual stresses mainly redistr...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	International journal of fatigue Ročník 110; s. 10 - 21
Hlavní autoři:	Klotz, T., Delbergue, D., Bocher, P., Lévesque, M., Brochu, M.
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Kidlington Elsevier Ltd 01.05.2018 Elsevier BV
Témata:	Aerospace industry Aircraft components Compressive properties Crack initiation Crack propagation Deformation Fatigue Fatigue cracks Fatigue failure Fatigue life Fatigue tests Fracture mechanics High cycle fatigue Inconel 718 Low cycle fatigue Materials fatigue Mechanical components Nickel base alloys Residual stress Residual stresses relaxation Shot peening Strain hardening Stress relaxation Superalloys Surface chemistry Surface properties Surface roughness dσcomp=0 E El XRD RSm σu Av σmin Nf εp Residual stresses relaxation σcomp,max Crack initiation σsurf Rt dσcomp,max σy0.2 Inconel 718 Fatigue Shot peening Bal AR Rσ β σmax LB 12S2 FWHM λ ν
ISSN:	0142-1123, 1879-3452
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!