CMAS corrosion characteristics of YSZ and Al2O3-YSZ thermal barrier coatings at 1250 °C–1350 °C

The calcium-magnesium-aluminum-silicate (CMAS) corrosion is now a great threat to thermal barrier coatings (TBCs), inducing coating spallation readily. The CMAS corrosion characteristics of both 7YSZ and 20 wt.%Al2O3-YSZ TBCs at a broad temperature range of 1250 °C to 1350 °C were investigated. 7YSZ...