Highly-durable plasma-sprayed Al2O3-YSZ/YSZ double ceramic layer TBCs against CMAS corrosion

The addition of Al2O3 inside thermal barrier coatings (TBCs) is highlighted effective on mitigating TBCs degradation induced by CMAS corrosion. In this study, the cost-effective 20 wt.%Al2O3-7YSZ/7YSZ double ceramic layer (DCL) TBCs were fabricated and their long-term performance resisting CMAS corr...