Low-firing, temperature stable and improved microwave dielectric properties of ZnO-TiO2-Nb2O5 composite ceramics

This article presents low-firing, low-loss and temperature stable ZnOTiO2Nb2O5 microwave dielectric composite ceramics with the assistance of lithium borosilicate (LBS) and zinc borosilicate (ZBS) glass frits. There is a liquid phase (eutectic mixture) generated by LBS (ZBS) glass, and solid parti...

Celý popis

Uložené v:
Podrobná bibliografia
Vydané v:Journal of Materiomics Ročník 5; číslo 3; s. 471 - 479
Hlavní autori: Yang, Hongyu, Zhang, Shuren, Chen, Yawei, Yang, Hongcheng, Fang, Zixuan, Yuan, Ying, Li, Enzhu
Médium: Journal Article
Jazyk:English
Vydavateľské údaje: Elsevier 01.09.2019
ISSN:2352-8478
On-line prístup:Získať plný text
Tagy: Pridať tag
Žiadne tagy, Buďte prvý, kto otaguje tento záznam!
Popis
Shrnutí:This article presents low-firing, low-loss and temperature stable ZnOTiO2Nb2O5 microwave dielectric composite ceramics with the assistance of lithium borosilicate (LBS) and zinc borosilicate (ZBS) glass frits. There is a liquid phase (eutectic mixture) generated by LBS (ZBS) glass, and solid particles could be wetted and dissolved. Therefore, the migrations and rearrangements of particles could be performed. Besides, compared with ceramics undoped with glass frits, lower activation energies (Ea) of ceramics doped with LBS and ZBS glass suggest that the low-temperature sintering behavior is easier to carry out. The results indicated that LBS and ZBS glass both are effective sintering aids to accelerate the sintering process and improve the microwave dielectric properties of composite ceramics by controlling the phase compositions under low temperature. Combination great properties of ZnOTiO2Nb2O5 ceramics were obtained when sintered at 900 °C for 4 h: εr = 36.7, Q × f = 20,000 GHz, τf = 7 ppm/oC. Keywords: ZnO-TiO2Nb2O5, Composite ceramics, Dielectric
ISSN:2352-8478
DOI:10.1016/j.jmat.2019.01.003