Study of mechanical character and corrosion properties of La2O3 nanoparticle reinforced Ni-W composite coatings

In this paper, Ni-W/La2O3 composite coatings were successfully prepared by pulse electrodeposition technology. The effect of the nano-La2O3 content in the plating solution on the structure and properties of the plated layers were evaluated. We find that nano-La2O3 can improve the situation of struct...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Colloids and surfaces. A, Physicochemical and engineering aspects Jg. 652; S. 129799
Hauptverfasser: Cheng, Xinyu, He, Yi, Song, Ruxia, Li, Hongjie, Liu, Bo, Zhou, Huilian, Yan, Liping
Format: Journal Article
Sprache:Englisch
Veröffentlicht: Elsevier B.V 05.11.2022
Schlagworte:
corrosion
Corrosion resistance
crystallites
Electrodeposition
electroplating
friction
Nano-lanthanum oxide
Ni-W/La2O3 composite coating
Nickel-tungsten composite coating
Nickel-tungsten composite coating
Corrosion resistance
Nano-lanthanum oxide
Electrodeposition
Ni-W/La2O3 composite coating
ISSN:0927-7757
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this paper, Ni-W/La2O3 composite coatings were successfully prepared by pulse electrodeposition technology. The effect of the nano-La2O3 content in the plating solution on the structure and properties of the plated layers were evaluated. We find that nano-La2O3 can improve the situation of structural defects such as microcracks in the coating and serve to increase the thickness of the coating. Meanwhile, the Ni-W/La2O3 (4 g‧L−1) composite coating has the smallest crystallite size (6.52 nm). Compared with the Ni-W composite coating, the microhardness of Ni-W/La2O3 (4 g‧L−1) composite coating increased by 38.61 % (the microhardness value is 682.30 Hv), while the friction coefficient decreased by 46.57 % (the average coefficient of friction is 0.246) and the corrosion rate decreased by 81.54 % (the corrosion rate is 0.0498 mm‧a−1). [Display omitted] •The hardness value of Ni-W/La2O3 (4 g‧L−1) composite coating increased by 38.61 %.•The COF of Ni-W/La2O3 (4 g‧L−1) composite coating decreased by 46.57 %.•The corrosion rate of Ni-W/La2O3 (4 g‧L−1) composite coating decreased by 81.54 %.
Bibliographie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 23
ISSN:0927-7757
DOI:10.1016/j.colsurfa.2022.129799