The intergrowth of YTa7O19 in L-Ta2O5 with Er3+/Yb3+ enhancing pure green upconversion luminescence intensity by molten salt synthesis

By using the molten salt synthesis with B2O3 flux and adjusting the doping concentration of Y3+, the intergrowth of the YTa7O19 phase in L-Ta2O5 is achieved. This structure enhances the pure green upconversion luminescence (UCL) intensity, which is because the YTa7O19 phase isolates the distribution...