Low-temperature strategy to synthesize highly ordered mesoporous silicas with very large pores

By employing a novel low-temperature synthetic pathway, highly ordered cubic mesoporous materials with hitherto the largest pores (up to 27 nm) and unit cells (up to 44 nm) have been successfully obtained.