Оценка вязкопластических свойств стали 09Г2С при испытаниях на растяжение
Uložené v:
| Názov: | Оценка вязкопластических свойств стали 09Г2С при испытаниях на растяжение |
|---|---|
| Autori: | Prokopeva, O. E., Ovsyannikov, A. B., Khotinov, V. A. |
| Informácie o vydavateľovi: | Издательский Дом «Ажур», 2025. |
| Rok vydania: | 2025 |
| Predmety: | FRACTURE SURFACE, КРИВЫЕ РАСТЯЖЕНИЯ, TENSILE CURVES, ПОВЕРХНОСТЬ РАЗРУШЕНИЯ, КОНСТРУКЦИОННЫЕ СТАЛИ, HEAT TREATMENT, STRUCTURAL STEELS, ТЕРМООБРАБОТКА, PLASTICITY, ПЛАСТИЧНОСТЬ |
| Popis: | The mechanical properties of 09G2S steel subjected to heat treatment under different modes have been investigated. A detailed analysis of the deformation behaviour of the steel samples during tensile tests was carried out, on the basis of which the parameters of tensile curves sensitive to the structural-phase state of the metal were identified. By the method of optical metallography the structure of steel was studied both in the heat-treated state and at different stages of tensile behaviour. As a result of analysis of the fractures of the samples after tensile stressing, a correlation between the mechanical properties and the fractographic parameters of fracture was revealed. Исследованы механические свойства стали 09Г2С, подвергнутой термообработке по различным режимам. Проведен детальный анализ деформационного поведения образцов исследуемой стали при испытаниях на растяжение, на основании которого выделены параметры кривых растяжения, чувствительные к структурно-фазовому состоянию металла. Методом оптической металлографии изучена структура стали как в термообработанном состоянии, так и на разных стадиях растяжения. В результате анализа изломов образцов после растяжения выявлена корреляция между механическими свойствами и фрактографическими параметрами разрушения. |
| Druh dokumentu: | Article |
| Popis súboru: | application/pdf |
| Jazyk: | Russian |
| Prístupová URL adresa: | http://elar.urfu.ru/handle/10995/142295 |
| Prístupové číslo: | edsair.od.......917..6c7ceb9ff60e684e7861a882c0216ecb |
| Databáza: | OpenAIRE |
Nájsť tento článok vo Web of Science | Abstrakt: | The mechanical properties of 09G2S steel subjected to heat treatment under different modes have been investigated. A detailed analysis of the deformation behaviour of the steel samples during tensile tests was carried out, on the basis of which the parameters of tensile curves sensitive to the structural-phase state of the metal were identified. By the method of optical metallography the structure of steel was studied both in the heat-treated state and at different stages of tensile behaviour. As a result of analysis of the fractures of the samples after tensile stressing, a correlation between the mechanical properties and the fractographic parameters of fracture was revealed.<br />Исследованы механические свойства стали 09Г2С, подвергнутой термообработке по различным режимам. Проведен детальный анализ деформационного поведения образцов исследуемой стали при испытаниях на растяжение, на основании которого выделены параметры кривых растяжения, чувствительные к структурно-фазовому состоянию металла. Методом оптической металлографии изучена структура стали как в термообработанном состоянии, так и на разных стадиях растяжения. В результате анализа изломов образцов после растяжения выявлена корреляция между механическими свойствами и фрактографическими параметрами разрушения. |
|---|