Evaluation of titanium dioxide and tantalum pentoxide nanoparticles for coating NiTi archwires in orthodontics: An in vitro study

Uloženo v:
Podrobná bibliografie
Název: Evaluation of titanium dioxide and tantalum pentoxide nanoparticles for coating NiTi archwires in orthodontics: An in vitro study
Autoři: Abeer B Mahmood, Akram F Alhuwaizi, Mohammed K Khalaf, Abbas R Zaher
Zdroj: Journal of Baghdad College of Dentistry, Vol 36, Iss 3 (2024)
Informace o vydavateli: Journal of Baghdad College of Dentistry, 2024.
Rok vydání: 2024
Témata: Nickel-titanium, Orthodontic archwires, Nanoparticle, atomic force microscopy, Dentistry, TiO2, Ta2O5, RK1-715
Popis: Background: This study aims to enhance the biocompatibility of Nickel–Titanium (NiTi) alloy by developing a new coating using titanium dioxide (TiO2) and titanium pentoxide (Ta2O5) through direct current (DC) reactive sputtering technology. Materials and methods: Two distinct coating materials, namely, TiO2 and Ta2O5, were used to fabricate NiTi orthodontic archwires with improved surface properties. TiO2 nanoparticles, with thickness ranging from 21.90 nm to 31.93 nm, were deposited onto NiTi alloy substrates through DC reactive sputtering deposition under different power conditions. Results: X-ray diffraction and field emission scanning electron microscopy validated the uniformity and morphology of the coatings. Immersion tests in simulated body fluid (SBF) revealed significant hydroxyapatite layer growth on TiO2-coated NiTi, especially at a sputtering power of 240 W. Reduced nickel ion release was observed on TiO2 nanoparticles with a thickness of 21.90 nm at 50 W sputtering power compared with 31.93 nm-thick nanoparticles at 240 W. Ta2O5 thin films were deposited on NiTi substrates through DC magnetron reactive sputtering at ~100 °C with a deposition power of 50 W. Structural and morphological analyses through optical microscopy and X-ray diffraction, atomic force microscopy, and scanning electron microscopy revealed the homogeneity and low roughness of the coatings. Biocompatibility assessments in artificial saliva and SBF solutions established that Ta2O5-coated NiTi alloys exhibited superior electrochemical behavior, enhanced corrosion resistance, and diminished Ni ion release compared with uncoated specimens. Conclusion: TiO2 and Ta2O5 coatings not only improved the biocompatibility of NiTi orthodontic archwires but also presented a promising path for advanced biomedical applications. These coatings have potential in improving the cellular behavior and performance of NiTi-based orthodontic devices.
Druh dokumentu: Article
ISSN: 2311-5270
1817-1869
DOI: 10.26477/jbcd.v36i3.3740
Přístupová URL adresa: https://doaj.org/article/76c9eba6e7014efab72501d89e375fd0
Rights: CC BY
Přístupové číslo: edsair.doi.dedup.....d21f9c504966c2fa7031f81f95a5bf6f
Databáze: OpenAIRE
Popis
Abstrakt:Background: This study aims to enhance the biocompatibility of Nickel–Titanium (NiTi) alloy by developing a new coating using titanium dioxide (TiO2) and titanium pentoxide (Ta2O5) through direct current (DC) reactive sputtering technology. Materials and methods: Two distinct coating materials, namely, TiO2 and Ta2O5, were used to fabricate NiTi orthodontic archwires with improved surface properties. TiO2 nanoparticles, with thickness ranging from 21.90 nm to 31.93 nm, were deposited onto NiTi alloy substrates through DC reactive sputtering deposition under different power conditions. Results: X-ray diffraction and field emission scanning electron microscopy validated the uniformity and morphology of the coatings. Immersion tests in simulated body fluid (SBF) revealed significant hydroxyapatite layer growth on TiO2-coated NiTi, especially at a sputtering power of 240 W. Reduced nickel ion release was observed on TiO2 nanoparticles with a thickness of 21.90 nm at 50 W sputtering power compared with 31.93 nm-thick nanoparticles at 240 W. Ta2O5 thin films were deposited on NiTi substrates through DC magnetron reactive sputtering at ~100 °C with a deposition power of 50 W. Structural and morphological analyses through optical microscopy and X-ray diffraction, atomic force microscopy, and scanning electron microscopy revealed the homogeneity and low roughness of the coatings. Biocompatibility assessments in artificial saliva and SBF solutions established that Ta2O5-coated NiTi alloys exhibited superior electrochemical behavior, enhanced corrosion resistance, and diminished Ni ion release compared with uncoated specimens. Conclusion: TiO2 and Ta2O5 coatings not only improved the biocompatibility of NiTi orthodontic archwires but also presented a promising path for advanced biomedical applications. These coatings have potential in improving the cellular behavior and performance of NiTi-based orthodontic devices.
ISSN:23115270
18171869
DOI:10.26477/jbcd.v36i3.3740