CHLORIDE DIFFUSION RATE IN LOADED FLY ASH CONCRETE USING STEADY-STATE MIGRATION TEST.

Uloženo v:
Podrobná bibliografie
Název: CHLORIDE DIFFUSION RATE IN LOADED FLY ASH CONCRETE USING STEADY-STATE MIGRATION TEST.
Autoři: Adiyastuti, Sri Murti, Pramayuda, Kemal, Ilman, Eko Charnius
Zdroj: International Journal of GEOMATE; Nov2025, Vol. 29 Issue 135, p50-57, 8p
Témata: DURABILITY, SUSTAINABILITY, MECHANICAL loads, CORROSION resistance, CONCRETE, NERNST-Planck equation, CONCRETE construction
Abstrakt: Chloride-induced corrosion is a major durability concern for concrete structures in marine environments, particularly under mechanical loading, as the resulting micro-cracking and cracking can accelerate chloride ingress, allowing these corrosive ions to reach the steel reinforcement more easily and compromise the structure's integrity. This study investigates the combined effect of mechanical pre-loading and fly ash replacement (0%, 20%, 30%, and 40%) on chloride diffusion in high-strength concrete. Sixteen concrete discs were tested using the NT Build 355 steady-state migration method for durations of 7 and 14 days. Before testing, a load of up to 2,000 kilograms was applied to eight specimens, while the remaining eight were left unloaded. The chloride diffusion coefficient was calculated using the Nernst-Planck equation. The results demonstrated that increasing fly ash content consistently reduced chloride ingress, with a maximum reduction of 79.8% observed in specimens with 40% fly ash under pre-loading conditions. These reductions were repeatable across both durations and fly ash percentages, with notably greater performance observed at 30% and 40% replacement compared to 20%. Replacing cement with 30–40% fly ash significantly enhances the durability and extends the service life of concrete structures in marine environments, even when subjected to pre-loading. Additionally, this approach contributes to sustainability by reducing cement consumption, which in turn lowers carbon dioxide emissions. [ABSTRACT FROM AUTHOR]
Copyright of International Journal of GEOMATE is the property of Geomate International Society and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Databáze: Complementary Index
Popis
Abstrakt:Chloride-induced corrosion is a major durability concern for concrete structures in marine environments, particularly under mechanical loading, as the resulting micro-cracking and cracking can accelerate chloride ingress, allowing these corrosive ions to reach the steel reinforcement more easily and compromise the structure's integrity. This study investigates the combined effect of mechanical pre-loading and fly ash replacement (0%, 20%, 30%, and 40%) on chloride diffusion in high-strength concrete. Sixteen concrete discs were tested using the NT Build 355 steady-state migration method for durations of 7 and 14 days. Before testing, a load of up to 2,000 kilograms was applied to eight specimens, while the remaining eight were left unloaded. The chloride diffusion coefficient was calculated using the Nernst-Planck equation. The results demonstrated that increasing fly ash content consistently reduced chloride ingress, with a maximum reduction of 79.8% observed in specimens with 40% fly ash under pre-loading conditions. These reductions were repeatable across both durations and fly ash percentages, with notably greater performance observed at 30% and 40% replacement compared to 20%. Replacing cement with 30–40% fly ash significantly enhances the durability and extends the service life of concrete structures in marine environments, even when subjected to pre-loading. Additionally, this approach contributes to sustainability by reducing cement consumption, which in turn lowers carbon dioxide emissions. [ABSTRACT FROM AUTHOR]