Effect of Induction Heating Temperature on the Microstructures and Properties of GH4169 Alloy.

Uloženo v:
Podrobná bibliografie
Název: Effect of Induction Heating Temperature on the Microstructures and Properties of GH4169 Alloy.
Autoři: Zhou, Haiping, Li, Jiliang, Zhang, Peng, Qin, Shengxue, Song, Tingting, Wei, Wenqing, Zhang, Hongbin, Liu, Jie, Chen, Shengchao
Zdroj: Journal of Materials Engineering & Performance; Jul2025, Vol. 34 Issue 13, p12641-12650, 10p
Témata: CRYSTAL grain boundaries, INDUCTION heating, RECRYSTALLIZATION (Metallurgy), CORROSION in alloys, TRANSMISSION electron microscopy
Abstrakt: The effect of induction heating temperature on the microstructures and properties of GH4169 nickel-based superalloy was investigated. Both electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) were applied to analyze the microstructure. The results showed that the induction heating temperature had a promoting influence on the evolution of static recrystallization (SRX) and the optimization of grain boundary characteristics distribution (GBCD). After induction heating, the coincidence site lattice (CSL) boundaries were mainly Σ3 boundaries, and the main formation mechanism was the growth accident model. With the increasing heating temperature, the SRX behavior was well developed with a gradual increase in the fraction of Σ3 boundaries. This indicates a 'symbiotic relationship' between the SRX grains and Σ3 boundaries. Moreover, it was found that the ductility and corrosion resistance of the alloy were improved with the increasing temperature. This is mainly due to the fact that the SRX behavior can effectively improve the uniformity of the microstructure and eliminate the residual stresses. Meanwhile, the high fraction of Σ3 boundaries disrupts the connectivity of the random grain boundary network, ultimately enhancing the corrosion resistance of the GH4169 alloy. [ABSTRACT FROM AUTHOR]
Copyright of Journal of Materials Engineering & Performance is the property of Springer Nature and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Databáze: Complementary Index
Popis
Abstrakt:The effect of induction heating temperature on the microstructures and properties of GH4169 nickel-based superalloy was investigated. Both electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) were applied to analyze the microstructure. The results showed that the induction heating temperature had a promoting influence on the evolution of static recrystallization (SRX) and the optimization of grain boundary characteristics distribution (GBCD). After induction heating, the coincidence site lattice (CSL) boundaries were mainly Σ3 boundaries, and the main formation mechanism was the growth accident model. With the increasing heating temperature, the SRX behavior was well developed with a gradual increase in the fraction of Σ3 boundaries. This indicates a 'symbiotic relationship' between the SRX grains and Σ3 boundaries. Moreover, it was found that the ductility and corrosion resistance of the alloy were improved with the increasing temperature. This is mainly due to the fact that the SRX behavior can effectively improve the uniformity of the microstructure and eliminate the residual stresses. Meanwhile, the high fraction of Σ3 boundaries disrupts the connectivity of the random grain boundary network, ultimately enhancing the corrosion resistance of the GH4169 alloy. [ABSTRACT FROM AUTHOR]