Transformations to the aluminum coordination environment and network polymerization in amorphous aluminosilicates under pressure.

Saved in:
Bibliographic Details
Title: Transformations to the aluminum coordination environment and network polymerization in amorphous aluminosilicates under pressure.
Authors: Gammond, Lawrence V. D., Zeidler, Anita, Youngman, Randall E., Fischer, Henry E., Bull, Craig L., Salmon, Philip S.
Source: Journal of Chemical Physics; 8/21/2024, Vol. 161 Issue 7, p1-21, 21p
Subject Terms: NUCLEAR magnetic resonance, NEUTRON diffraction, STRUCTURAL models, ALUMINUM silicates, CHEMICAL speciation
Abstract: The structure of calcium aluminosilicate glasses (CaO)x(Al2O3)y(SiO2)1−x−y with the near tectosilicate compositions x ≃ 0.19 and 1 − x − y ≃ 0.61 or x ≃ 0.26 and 1 − x − y ≃ 0.49 was investigated by in situ high-pressure neutron diffraction and 27Al nuclear magnetic resonance (NMR) spectroscopy. The results show three distinct pressure regimes for the transformation of the aluminum coordination environment from tetrahedral to octahedral, which map onto the deformations observed in the production of permanently densified materials. The oxygen packing fraction serves as a marker for signaling a change to the coordination number of the network forming motifs. For a wide variety of permanently densified aluminosilicates, the aluminum speciation shares a common dependence on the reduced density ρ′ = ρ/ρ0, where ρ is the density and ρ0 is its value for the uncompressed material. The observed increase in the Al–O coordination number with ρ′ originates primarily from the formation of six-coordinated aluminum Al(VI) species, the fraction of which increases rapidly beyond a threshold ρ thr ′ ∼ 1.1. The findings are combined to produce a self-consistent model for pressure-induced structural change. Provided the glass network is depolymerized, one-coordinated non-bridging oxygen atoms are consumed to produce two-coordinated bridging oxygen atoms, thus increasing the network connectivity in accordance with the results from 17O NMR experiments. Otherwise, three-coordinated oxygen atoms or triclusters appear, and their fraction is quantified by reference to the mean coordination number of the silicon plus aluminum species. The impact of treating Al(VI) as a network modifier is discussed. [ABSTRACT FROM AUTHOR]
Copyright of Journal of Chemical Physics is the property of American Institute of Physics and its content may not be copied or emailed to multiple sites without the copyright holder's express written permission. Additionally, content may not be used with any artificial intelligence tools or machine learning technologies. However, users may print, download, or email articles for individual use. This abstract may be abridged. No warranty is given about the accuracy of the copy. Users should refer to the original published version of the material for the full abstract. (Copyright applies to all Abstracts.)
Database: Complementary Index
Description
Abstract:The structure of calcium aluminosilicate glasses (CaO)<subscript>x</subscript>(Al<subscript>2</subscript>O<subscript>3</subscript>)<subscript>y</subscript>(SiO<subscript>2</subscript>)<subscript>1−x−y</subscript> with the near tectosilicate compositions x ≃ 0.19 and 1 − x − y ≃ 0.61 or x ≃ 0.26 and 1 − x − y ≃ 0.49 was investigated by in situ high-pressure neutron diffraction and <sup>27</sup>Al nuclear magnetic resonance (NMR) spectroscopy. The results show three distinct pressure regimes for the transformation of the aluminum coordination environment from tetrahedral to octahedral, which map onto the deformations observed in the production of permanently densified materials. The oxygen packing fraction serves as a marker for signaling a change to the coordination number of the network forming motifs. For a wide variety of permanently densified aluminosilicates, the aluminum speciation shares a common dependence on the reduced density ρ′ = ρ/ρ<subscript>0</subscript>, where ρ is the density and ρ<subscript>0</subscript> is its value for the uncompressed material. The observed increase in the Al–O coordination number with ρ′ originates primarily from the formation of six-coordinated aluminum Al(VI) species, the fraction of which increases rapidly beyond a threshold ρ thr ′ ∼ 1.1. The findings are combined to produce a self-consistent model for pressure-induced structural change. Provided the glass network is depolymerized, one-coordinated non-bridging oxygen atoms are consumed to produce two-coordinated bridging oxygen atoms, thus increasing the network connectivity in accordance with the results from <sup>17</sup>O NMR experiments. Otherwise, three-coordinated oxygen atoms or triclusters appear, and their fraction is quantified by reference to the mean coordination number of the silicon plus aluminum species. The impact of treating Al(VI) as a network modifier is discussed. [ABSTRACT FROM AUTHOR]