Platinum particle size and support effects in NO(x) mediated carbon oxidation over platinum catalysts

Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AIPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream co...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Environmental science & technology Ročník 40; číslo 8; s. 2727
Hlavní autoři: Villani, Kenneth, Vermandel, Walter, Smets, Koen, Liang, Duoduo, van Tendeloo, Gustaaf, Martens, Johan A
Médium: Journal Article
Jazyk:angličtina
Vydáno: United States 15.04.2006
Témata:
Air Pollution - prevention & control
Carbon - chemistry
Catalysis
Nitric Oxide - chemistry
Oxidation-Reduction
Particle Size
Platinum - chemistry
Porosity
Titanium
Zeolites - chemistry
ISSN:0013-936X
On-line přístup:Zjistit podrobnosti o přístupu
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:Platinum metal was dispersed on microporous, mesoporous, and nonporous support materials including the zeolites Na-Y, Ba-Y, Ferrierite, ZSM-22, ETS-10, and AIPO-11, alumina, and titania. The oxidation of carbon black loosely mixed with catalyst powder was monitored gravimetrically in a gas stream containing nitric oxide, oxygen, and water. The carbon oxidation activity of the catalysts was found to be uniquely related to the Pt dispersion and little influenced by support type. The optimum dispersion is around 3-4% corresponding to relatively large Pt particle sizes of 20-40 nm. The carbon oxidation activity reflects the NO oxidation activity of the platinum catalyst, which reaches an optimum in the 20-40 nm Pt particle size range. The lowest carbon oxidation temperatures were achieved with platinum loaded ZSM-22 and AIPO-11 zeolite crystallites bearing platinum of optimum dispersion on their external surfaces.
Bibliografie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 23
ISSN:0013-936X
DOI:10.1021/es051871h