ZrSi2–MgO as novel additives for high thermal conductivity of β‐Si3N4 ceramics

A novel ZrSi2–MgO system was used as sintering additive for fabricating high thermal conductivity silicon nitride ceramics by gas pressure sintering at 1900°C for 12 hours. By keeping the total amount of additives at 7 mol% and adjusting the amount of ZrSi2 in the range of 0‐7 mol%, the effect of Zr...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	Journal of the American Ceramic Society Ročník 103; číslo 3; s. 2090 - 2100
Hlavní autoři:	Wang, Weide, Yao, Dongxu, Chen, Huanbei, Xia, Yongfeng, Zuo, Kaihui, Yin, Jinwei, Liang, Hanqin, Zeng, Yu‐Ping
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Columbus Wiley Subscription Services, Inc 01.03.2020
Témata:	Additives Ceramics Densification Dilatometry Gas pressure Grain boundaries Grain growth Heat conductivity Heat transfer Hot pressing Liquid phases Magnesium oxide Silicon dioxide Silicon nitride Sintering Thermal conductivity Zirconium dioxide ZrSi2
ISSN:	0002-7820, 1551-2916
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!