Macrocellular Titanosilicate Monoliths as Highly Efficient Structured Olefin Epoxidation Catalysts

Self‐standing macrocellular titanosilicate monolith foams are obtained using a one‐pot sol‐gel route and show excellent performance in the epoxidation of cyclohexene. Thanks to the High Internal Phase Emulsion (HIPE) templating method, the materials feature a high void fraction, a hierarchically por...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:ChemCatChem Ročník 11; číslo 6; s. 1593 - 1597
Hlavní autoři: Smeets, Valentin, van den Biggelaar, Ludivine, Barakat, Tarek, Gaigneaux, Eric M., Debecker, Damien P.
Médium: Journal Article
Jazyk:angličtina
Vydáno: Weinheim Wiley Subscription Services, Inc 20.03.2019
Témata:
Catalysis
Continuous flow
Cyclohexene
cyclohexene epoxidation
Epoxidation
High Internal Phase Emulsion
monolith foam
Plastic foam
Silicon dioxide
Sol-gel processes
titanosilicate
Void fraction
ISSN:1867-3880, 1867-3899
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:Self‐standing macrocellular titanosilicate monolith foams are obtained using a one‐pot sol‐gel route and show excellent performance in the epoxidation of cyclohexene. Thanks to the High Internal Phase Emulsion (HIPE) templating method, the materials feature a high void fraction, a hierarchically porous texture and good mechanical strength. Highly dispersed Ti species can be incorporated in tetrahedral coordination in the silica matrix. These characteristics allow the obtained ‘SiTi(HIPE)’ materials to reach high catalytic turnover in the epoxidation of cyclohexene. The monoliths can advantageously be used to run the reaction in continuous flow mode. Hype the HIPE: Self‐standing titanosilicate monolith foams obtained using the High Internal Phase Emulsion (HIPE) templating method, present hierarchical porosity, high Ti dispersion, and reach high TOF in the epoxidation of cyclohexene. A flow‐mode olefin epoxidation process is demonstrated.
Bibliografie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:1867-3880
1867-3899
DOI:10.1002/cctc.201900028