Vegetable Oil-Based Resins Reinforced with Spruce Bark Powder and with Its Hydrochar Lignocellulosic Biomass

A bio-based polymeric matrix was developed by the copolymerization of a vegetable oil-based epoxy, epoxidized linseed oil (ELO), with dodecenyl succinic anhydride (DDSA). To obtain eco-friendly bio-composites, this matrix was combined with a natural filler: spruce bark powder (SB) with its hydrochar...

Celý popis

Uložené v:
Podrobná bibliografia
Vydané v:Applied sciences Ročník 11; číslo 22; s. 10649
Hlavní autori: Dinu, Roxana, Bejenari, Iuliana, Volf, Irina, Mija, Alice
Médium: Journal Article
Jazyk:English
Vydavateľské údaje: Basel MDPI AG 01.11.2021
Multidisciplinary digital publishing institute (MDPI)
Predmet:
bio-composite
Biomass
Bisphenol A
Chemical Sciences
Composite materials
Curing
Epoxy resins
hydrothermal carbon
Lignocellulose
Raw materials
sustainable materials
vegetable oil
Vegetable oils
ISSN:2076-3417, 2076-3417
On-line prístup:Získať plný text
Tagy: Pridať tag
Žiadne tagy, Buďte prvý, kto otaguje tento záznam!
Popis
Shrnutí:A bio-based polymeric matrix was developed by the copolymerization of a vegetable oil-based epoxy, epoxidized linseed oil (ELO), with dodecenyl succinic anhydride (DDSA). To obtain eco-friendly bio-composites, this matrix was combined with a natural filler: spruce bark powder (SB) with its hydrochar (HC) in various proportions ranged from 1 to 30 wt.%. The reactivities of these formulations were studied by DSC analysis that highlighted that both fillers have a high catalytic effect on the ELO–DDSA crosslinking reaction. The complementary studies by TGA, DMA, tensile tests, water absorption and Shore tests had shown that both HC and SB bring improvements to the mechanical properties of the composites, fulfilling multiple roles: (i) Both act as co-reactants in the copolymerization mechanism; (ii) HC acts as reinforcement, consolidating the network and providing stiffness and rigidity; and (iii) SB acts as plasticizer for reducing the brittle character of the epoxy resins.
Bibliografia:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:2076-3417
2076-3417
DOI:10.3390/app112210649