Effects of annealing on the microstructure and mechanical properties of selective laser melted AlSi7Mg alloy

Selective laser melting, due to the high energy density input and the small interaction time (106 K/s), can result in an ultrafine microstructure and excellent mechanical properties. However, due to the nonuniform nature of the temperature distribution and the transition from liquid to solid, high r...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	Materials science & engineering. A, Structural materials : properties, microstructure and processing Ročník 739; s. 463 - 472
Hlavní autoři:	Wang, Min, Song, Bo, Wei, Qingsong, Zhang, Yuanjie, Shi, Yusheng
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Lausanne Elsevier B.V 02.01.2019 Elsevier BV
Témata:	Alloys Aluminum base alloys Annealing Diamond pyramid hardness Dimpling Ductile fracture Ductile-brittle transition Elongation Flux density Fracture mechanics Laser beam melting Mechanical properties Microstructure Morphology Residual stress Residual stresses Selective laser melting Temperature distribution Tensile stress Ultrafines Mechanical properties Annealing Residual stresses Selective laser melting
ISSN:	0921-5093, 1873-4936
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!