Enhancement of bending strength properties of two wood species reinforced with two types of carbon fibre fabrics and two layouts

This work examined the enhancement of bending strength properties of two wood species, namely fir and pine, reinforced with two carbon fibre fabrics (CFF) of different areal weight, in two different layouts. CFF applied in the bottom surfaces of the specimens ('F'-type) and in the second w...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:International Wood Products Journal Ročník 11; číslo 2; s. 64 - 69
Hlavní autoři: Karastergiou, Sotirios, Foti, Dafni, Filippou, Vasileios, Papadopoulos, Antonios
Médium: Journal Article
Jazyk:angličtina
Vydáno: London, England Taylor & Francis 02.04.2020
SAGE Publications
Témata:
Abies
areal weight
bending properties
bending strength
carbon fibers
carbon fibre
Composites
fabrics
fibre-reinforced plastic
glass fibre
layouts
Pinus
reinforcement
weight
wood
Composites
carbon fibre
glass fibre
reinforcement
bending properties
fibre-reinforced plastic
layouts
areal weight
ISSN:2042-6445, 2042-6453, 2042-6453
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:This work examined the enhancement of bending strength properties of two wood species, namely fir and pine, reinforced with two carbon fibre fabrics (CFF) of different areal weight, in two different layouts. CFF applied in the bottom surfaces of the specimens ('F'-type) and in the second wrapped in the bottom surfaces and up to the half of the lateral surfaces ('U'-type).The results indicated that samples which are reinforced with CCF show higher MOR and MOE values than the controls and this improvement was found to be significantly different. The reinforcement layout affected the bending properties of both pine and fir wood, since the corresponding values are higher in U-shaped reinforcement than in F-type reinforcement, at identical CFF areal weights. In the case of fir wood, the CFF areal weight did not significantly affect the bending properties.
Bibliografie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 23
ISSN:2042-6445
2042-6453
2042-6453
DOI:10.1080/20426445.2020.1729497