Effect of voids on fatigue damage propagation in 3D5D braided composites revealed via automated algorithms using X-ray computed tomography

[Display omitted] •Significant advancement has been the combination of Micro-CT and novel image algorithms to track the 3D deflection of individual voids.•For the larger voids, the speed of crack propagation is higher and reaches saturation before 76.9% of life.•Debonding still dominates the fatigue...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	International journal of fatigue Ročník 158; s. 106778
Hlavní autoři:	Liu, Xiaodong, Wang, Xiaoxu, Zhang, Diantang, Qian, Kun
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Kidlington Elsevier Ltd 01.05.2022 Elsevier BV
Témata:	3-Dimensional reinforcement Algorithms Automation Braided composites Coalescing Computed tomography Cracking (fracturing) CT analysis Damage Damage propagation Defects Fatigue Fatigue failure Fatigue life Fatigue tests Fracture mechanics Life prediction Materials fatigue Prediction models Propagation Three dimensional composites Voids Yarns 3-Dimensional reinforcement Fatigue CT analysis Damage propagation Defects
ISSN:	0142-1123, 1879-3452
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!