Kinetic Characteristics of Nitriding of Zr–1% Nb Alloy

We study the kinetic characteristics of nitriding of thin-sheet (~ 1 mm) samples of Zr–1% Nb alloy treated in a nitrogen atmosphere ( ) in broad temperature ( T = 550; 650; 750; 850 and 950°С) and time ( τ = 1; 5 and 10 h) ranges. It is shown that the process of nitriding of the analyzed alloy obeys...

Celý popis

Uložené v:
Podrobná bibliografia
Vydané v:Materials science (New York, N.Y.) Ročník 58; číslo 3; s. 408 - 416
Hlavní autori: Trush, V. S., Pohrelyuk, I. M., Kravchyshyn, T. M., Luk’yanenko, A. G., Stoev, P. I., Fedirko, V. M., Kovalchuk, I. V.
Médium: Journal Article
Jazyk:English
Vydavateľské údaje: New York Springer US 01.11.2022
Springer
Springer Nature B.V
Predmet:
Alloys
Characterization and Evaluation of Materials
Chemistry and Materials Science
Materials Science
Microhardness
Niobium base alloys
Nitriding
Nitrogen
Reflexes
Solid Mechanics
Specialty metals industry
Structural Materials
Zirconium base alloys
Zr–1% Nb alloy
microstructure
surface layer
parameters of the crystal lattice
kinetics of mass changes
microhardness
nitriding
ISSN:1068-820X, 1573-885X
On-line prístup:Získať plný text
Tagy: Pridať tag
Žiadne tagy, Buďte prvý, kto otaguje tento záznam!
Popis
Shrnutí:We study the kinetic characteristics of nitriding of thin-sheet (~ 1 mm) samples of Zr–1% Nb alloy treated in a nitrogen atmosphere ( ) in broad temperature ( T = 550; 650; 750; 850 and 950°С) and time ( τ = 1; 5 and 10 h) ranges. It is shown that the process of nitriding of the analyzed alloy obeys a law close to a parabolic dependence ( n ≈ 2). It is discovered that the activation energy of nitriding of the alloy within the temperature range 550–950°C is equal to 131.8 kJ/mole. The microstructure of the subsurface layer of the alloy after nitriding is analyzed. The distribution of the surface microhardness of Zr–1% Nb alloy is determined. The diagrams of intensity of the phase reflexes of α -Zr and ZrN on the surface of alloy after treatment in a nitrogen atmosphere are constructed.
Bibliografia:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:1068-820X
1573-885X
DOI:10.1007/s11003-023-00678-2