The effect of laser shock peening, shot peening and their combination on the microstructure and fatigue properties of Ti-6Al-4V titanium alloy

[Display omitted] •The fatigue life can be significantly improved (up to 9.3 times) by (LSP+SP).•Gradient microstructure with dislocations and novel CRS distribution can be induced.•Fatigue crack initiation can be hindered by the high-density dislocation layer.•Fatigue crack growth rate can be retar...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	International journal of fatigue Ročník 153; s. 106465
Hlavní autoři:	Luo, Xuekun, Dang, Ning, Wang, Xin
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Kidlington Elsevier Ltd 01.12.2021 Elsevier BV
Témata:	Compressive properties Crack initiation Crack propagation Dislocation density Fatigue failure Fatigue life Fractography Fracture mechanics Laser shock processing Materials fatigue Metal fatigue Microstructure Microstructures Residual stress Residual stresses Shot peening Surface treatments Titanium alloys Titanium base alloys Surface treatments Shot peening Microstructures Residual stresses Fractography
ISSN:	0142-1123, 1879-3452
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!