Fatigue behavior of AW7075 aluminum alloy in ultra-high cycle fatigue region

Advanced electron microscopy methods were used with the aim to explain the differences in the response of strengthened AW 7075 – T6511 aluminum alloy to fatigue loading at 5 Hz and 20 kHz. The shift of the S–N curve to higher number of cycles to fracture for the specimens tested at high frequency wa...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	Materials science & engineering. A, Structural materials : properties, microstructure and processing Ročník 774; s. 138922
Hlavní autoři:	Fintová, S., Kuběna, I., Trško, L., Horník, V., Kunz, L.
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Lausanne Elsevier B.V 13.02.2020 Elsevier BV
Témata:	Aluminum alloys Aluminum base alloys AW7075 Crack initiation Crack propagation Cyclic loads Dislocation density Fatigue Fatigue crack initiation Fatigue damage Fatigue failure Fracture mechanics High cycle fatigue Metal fatigue Ultra-high cycle fatigue Fatigue Ultra-high cycle fatigue AW7075 Fatigue damage Fatigue crack initiation
ISSN:	0921-5093, 1873-4936
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!