The enhanced performance of capacitive-type humidity sensors based on ZnO nanorods/WS2 nanosheets heterostructure

•The novel capacitive-type humidity sensor based on ZnO nanorods/WS2 nanosheets heterostructure was proposed.•The presence of WS2 increased the response and sensitivity and lowered the hysteresis without impacting response and recovery times.•The improved sensor performance might be due to the abili...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Sensors and actuators. B, Chemical Ročník 310; s. 127810 - 11
Hlavní autoři: Dwiputra, Muhammad Adam, Fadhila, Farah, Imawan, Cuk, Fauzia, Vivi
Médium: Journal Article
Jazyk:angličtina
Vydáno: Lausanne Elsevier B.V 01.05.2020
Elsevier Science Ltd
Témata:
Adsorption
Capacitance
Charge density
Coated electrodes
Control stability
Electric fields
Glass substrates
Heterostructures
Humidity
Humidity sensor
Hysteresis
Indium tin oxides
Morphology
N-n junctions
N-type semiconductors
Nanorods
Nanosheets
Performance enhancement
Room temperature
Sensors
Surface stability
Thermal stability
Tungsten disulfide
Two-dimensional
Water chemistry
WS2 nanosheets
Zinc oxide
Zinc oxides
ZnO
Humidity sensor
Capacitance
WS2 nanosheets
ZnO
Two-dimensional
ISSN:0925-4005, 1873-3077
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:•The novel capacitive-type humidity sensor based on ZnO nanorods/WS2 nanosheets heterostructure was proposed.•The presence of WS2 increased the response and sensitivity and lowered the hysteresis without impacting response and recovery times.•The improved sensor performance might be due to the ability of WS2 to provide more water molecule adsorption sites.•The interface of ZnO/WS2 contains high local charge density and an internal electric field that increase the water dissociation rate. Zinc oxide (ZnO) is a promising candidate for humidity-sensing materials due to its low-cost preparation, superior chemical and thermal stability, controllable surface morphology, and low water solubility. However, pristine ZnO-based humidity sensors suffer from poor response and large hysteresis that limit their application. In this study, n-type semiconducting tungsten disulfide (WS2) was utilized to form ZnO nanorods/WS2 nanosheets heterostructure grown on indium tin oxide coplanar electrode-coated glass substrate. The capacitive-type humidity sensing characteristics were investigated at room temperature. The results show that for humidity ranges of 18–85 % RH, three deposition cycles of WS2 nanosheets onto ZnO nanorods produced significant improvements in the response, sensitivity, and hysteresis with an unchanged response and recovery times compared to pristine ZnO sensors. This improved sensor performance might be due to the ability of WS2 to provide more water molecule adsorption sites. The formation of an n-n junction between ZnO and WS2 created interfaces with high local charge density and built an internal electric field that increase the water dissociation rate. The improved hysteresis might be due to water molecule adsorption on WS2 nanosheets is physical adsorption that facilitates the desorption process.
Bibliografie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:0925-4005
1873-3077
DOI:10.1016/j.snb.2020.127810