Highly-durable plasma-sprayed Al2O3-YSZ/YSZ double ceramic layer TBCs against CMAS corrosion

The addition of Al2O3 inside thermal barrier coatings (TBCs) is highlighted effective on mitigating TBCs degradation induced by CMAS corrosion. In this study, the cost-effective 20 wt.%Al2O3-7YSZ/7YSZ double ceramic layer (DCL) TBCs were fabricated and their long-term performance resisting CMAS corr...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Journal of the European Ceramic Society Ročník 44; číslo 12; s. 7328 - 7338
Hlavní autoři: Zhang, Yongang, Gao, Wei, Dou, Mengfan, Han, Jiasen, Wu, Dongting, Zou, Yong
Médium: Journal Article
Jazyk:angličtina
Vydáno: Elsevier Ltd 01.09.2024
Témata:
Al2O3-7YSZ composite coating
CMAS corrosion
Double ceramic layer
Thermal barrier coating
CMAS corrosion
Al2O3-7YSZ composite coating
Double ceramic layer
Thermal barrier coating
ISSN:0955-2219
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:The addition of Al2O3 inside thermal barrier coatings (TBCs) is highlighted effective on mitigating TBCs degradation induced by CMAS corrosion. In this study, the cost-effective 20 wt.%Al2O3-7YSZ/7YSZ double ceramic layer (DCL) TBCs were fabricated and their long-term performance resisting CMAS corrosion was investigated. Significant bending and CMAS infiltration occurred readily for the single layer 7YSZ coatings just after 5 h duration. The top sacrificial Al2O3-7YSZ layer of DCL coatings greatly constrained coating deflection and CMAS infiltration. This is due to the chemical reaction between alumina splats and CMAS, generating interconnected anorthites for effectively blocking CMAS infiltration and improving resistance to CMAS attack. However, it is highlighted that the role of alumina splats on mitigating CMAS degradation was found different between the short-term corrosion and long-term corrosion. In addition, interfacial delamination/cracking was not observed between the top Al2O3-7YSZ layer and bottom 7YSZ layer after 100 h CMAS corrosion, demonstrating superior interface integrity and durability.
ISSN:0955-2219
DOI:10.1016/j.jeurceramsoc.2024.05.020