Gradient residual stress evolution and its influence on fatigue life under combined carburising heat treatment and ultrasonic surface rolling process

•Carburizing heat treatment (CHT) combined with ultrasonic surface rolling process (USRP) were introduced to improve the rotary-bending fatigue behavior.•Rotary-bending fatigue life and surface integrity were improved after combined treatment (CHT + USRP).•The mechanism of gradient compressive resid...

Celý popis

Podrobná bibliografie

Vydáno v:	Engineering fracture mechanics Ročník 308; s. 110315
Hlavní autoři:	Wang, Gang, Hou, Xiaofan, Zhang, Yue, Peng, Zhenlong, Xu, Guangtao, Zhao, Minghao
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Elsevier Ltd 20.09.2024
Témata:	Carburising heat treatment Evolution mechanism Fatigue Gradient residual stress evolution Ultrasonic surface rolling process Fatigue Ultrasonic surface rolling process Evolution mechanism Carburising heat treatment Gradient residual stress evolution
ISSN:	0013-7944
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!