Oligopeptide‐Induced Multifunctional Interface Layer with Protonated Hydrophobic Behavior and Strong Affinity for Highly Stable Zinc Anode

Zinc‐ion batteries (ZIBs) have attracted wide attention due to their low redox potential, high capacity, and intrinsic safety. However, key issues such as zinc dendrite growth, corrosion, and passivation on zinc anode detrimentally affect the electrochemical performance. Herein, as proof of a concep...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	Advanced functional materials Ročník 35; číslo 21
Hlavní autoři:	Liang, Xiao, Yang, Rui, Zheng, Yongping, Zhang, Fan, Zhang, Wenjun, Lee, Chun‐Sing, Tang, Yongbing
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	Hoboken Wiley Subscription Services, Inc 01.05.2025
Témata:	Activated carbon Ammonia Capacitors Corrosion Cycles Electrochemical analysis Electrodes Electrolytes Functional groups Glutathione Hydrophobicity oligopeptide protonated interface layer Zinc zinc anode Zn‐ion energy storage devices
ISSN:	1616-301X, 1616-3028
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!