Improving CMAS-corrosion resistance of YSZ-based thermal barrier coatings with Al2O3 addition

Thermal barrier coatings (TBCs), exposed to the molten calcium‑magnesium‑aluminum-silicate (CMAS) deposits, could become degraded more readily during service. In this paper, the composite Al2O3/YSZ TBCs with different Al2O3 additions were prepared through the atmospheric plasma spraying technique an...