Facile fabrication of Au/SiO2 nanostructures from 1D to 3D nanotubes networks using templating methods

We report a facile fabrication method for free-standing gold (Au) or silica (SiO2) nanotubes with highly controlled geometry and ordered porosity (pNTs) and their nanostructuration from 1D to 3D interconnected networks. A dual nano-templating method was employed using polycarbonate membranes as firs...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Catalysis today Ročník 429; s. 114472
Hlavní autoři: Drault, Fabien, Eloy, Pierre, Demoustier-Champagne, Sophie, Hermans, Sophie
Médium: Journal Article
Jazyk:angličtina
Vydáno: Elsevier B.V 01.03.2024
Témata:
Dual-templates method
Electroless plating
Gold nanoparticles
Interconnected porous nanotube networks
Silica nanotubes
Sol-gel deposition
Interconnected porous nanotube networks
Electroless plating
Gold nanoparticles
Sol-gel deposition
Dual-templates method
Silica nanotubes
ISSN:0920-5861, 1873-4308
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:We report a facile fabrication method for free-standing gold (Au) or silica (SiO2) nanotubes with highly controlled geometry and ordered porosity (pNTs) and their nanostructuration from 1D to 3D interconnected networks. A dual nano-templating method was employed using polycarbonate membranes as first mold for the nanotubes, together with stacked polystyrene (PS) nanospheres to induce porosity. The pore size in the final nanotube walls can be controlled by adjusting the ratio x (where x = internal diameter of the nanotube divided by the diameter of the nanospheres), which determines the packing order of the spheres in the tubes. Then, gold electroless or silica sol-gel deposition were performed in the dual-templated structure to obtain Au or SiO2 pNTs, respectively. The templates removal was performed in one step using dichloromethane. A further functionalization of the silica pNTs with Au NPs using the electroless deposition method was successfully implemented as well, leading to a homogeneous dispersion of Au NPs with a size of 11 ± 2.8 nm. Chemical compositions and optical properties of the so-obtained materials were determined by XPS and UV–visible analyses, respectively. [Display omitted]
ISSN:0920-5861
1873-4308
DOI:10.1016/j.cattod.2023.114472