Disclosing the nature of vacancy defects in α-Ag2WO4

•Alteration of α-Ag2WO4 defects as a function of temperature.•Photoluminescence spectroscopy as a tool to evaluate oxygen vacancies.•Impedance spectroscopy and PALS as a tool to evaluate complex vacancies. Defects at semiconductors with electron acceptor and donor sites govern the electronic and opt...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Materials research bulletin Ročník 164; s. 112252
Hlavní autoři: Assis, M., Castro, M.S., Aldao, C.M., Buono, C., Ortega, P.P., Teodoro, M.D., Andrés, J., Gouveia, A.F., Simões, A.Z., Longo, E., Macchi, C.E., Somoza, A., Moura, F., Ponce, M.A.
Médium: Journal Article
Jazyk:angličtina
Vydáno: Elsevier Ltd 01.08.2023
Témata:
Defects
Electronic properties
α-Ag2WO4
α-Ag2WO4
Electronic properties
Defects
ISSN:0025-5408, 1873-4227
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:•Alteration of α-Ag2WO4 defects as a function of temperature.•Photoluminescence spectroscopy as a tool to evaluate oxygen vacancies.•Impedance spectroscopy and PALS as a tool to evaluate complex vacancies. Defects at semiconductors with electron acceptor and donor sites govern the electronic and optoelectronic applications due to their unique electronic properties. This work provides deep insight into the nature of defects and the conduction mechanism in α-Ag2WO4. To this aim, a detailed analysis of the results of XRD with Rietveld refinements, FE-SEM images, and measurements of different spectroscopies (impedance, positron annihilation lifetime, and photoluminescence) are carried out on α-Ag2WO4 samples synthesized by a simple co-precipitation method. Two types of vacancy defects: cationic O-vacancies, and anionic Ag or Ag–O vacancy complexes are elucidated with a Schottky p-type potential barrier. The results indicate that the Ag vacancies remain constant during thermal treatment, while an opposite effect is found for the oxygen vacancies. This behavior governs the multifunctional properties of α-Ag2WO4 semiconductors via a tunneling plus thermionic conduction mechanism. [Display omitted]
ISSN:0025-5408
1873-4227
DOI:10.1016/j.materresbull.2023.112252