Development of novel temperature-stable Al2O3–TiO2-based dielectric ceramics featuring superior thermal conductivity for LTCC applications

A new composition was developed using sintering to improve the dielectric properties of low-temperature co-fired alumina (LTCA) containing CuO–TiO2–Nb2O5–Ag2O. By substituting some alumina with rutile TiO2, the second-phase compound could be changed from AgNbO3 to the rutile phase. Further, low-temp...

Celý popis

Uložené v:

Podrobná bibliografia
Vydané v:	Journal of the European Ceramic Society Ročník 41; číslo 1; s. 376 - 386
Hlavní autori:	Shigeno, Koichi, Li, Moyuan, Fujimori, Hirotaka
Médium:	Journal Article
Jazyk:	English
Vydavateľské údaje:	Elsevier Ltd 01.01.2021
Predmet:	Al2O3 Low-Temperature co-fired ceramics (LTCCs) Microwave dielectric Property Thermal conductivity TiO2 LTCA LTCC XRD Low-Temperature co-fired ceramics (LTCCs) Al2O3 EDS Microwave dielectric TCE Thermal conductivity PVA XPS TEM Property FIB TiO2
ISSN:	0955-2219, 1873-619X
On-line prístup:	Získať plný text
Tagy:	Pridať tag Žiadne tagy, Buďte prvý, kto otaguje tento záznam!

Buďte prvý, kto okomentuje tento záznam!