Effect of Metallic Nanocoatings Deposited on Silicon Oxide on Wetting by Filler Melts I. Wetting of Ti, Nb, Cr, V, and Mo Nanocoatings Deposited on SiO2 with Filler Melts

The effect of metallic nanocoatings on the wetting of silicon oxide with lead-based filler melts (Pb–15 wt.% In and Pb–2.5 wt.% Ag) was studied by the sessile drop method with capillary cleaning of the melt in 1 ∙ 10 –3 Pa vacuum at 500°C. The dependence of the contact angle between the filler melt...

Celý popis

Uložené v:

Podrobná bibliografia
Vydané v:	Powder metallurgy and metal ceramics Ročník 59; číslo 1-2; s. 29 - 34
Hlavní autori:	Krasovskyy, V. P., Kostyuk, B. D., Gab, I. I., Krasovskaya, N. A., Stetsyuk, T. V.
Médium:	Journal Article
Jazyk:	English
Vydavateľské údaje:	New York Springer US 01.05.2020 Springer Nature B.V
Predmet:	Adhesive bonding Adhesives Affinity Automotive parts Ceramics Characterization and Evaluation of Materials Chemistry and Materials Science Chromium Composites Contact angle Contact melting Copper Glass Lead Materials Science Melts Metal coatings Metal oxides Metallic Materials Molybdenum Nanostructured Materials Natural Materials Niobium Oxide coatings Sessile drop method Silicon dioxide Silicon oxides Substrates Thickness Titanium Vanadium Wettability Wetting silicon oxide ‘threshold’ coating thickness wetting metal nanocoatings immobilization of nanostructured metallic coatings
ISSN:	1068-1302, 1573-9066
On-line prístup:	Získať plný text
Tagy:	Pridať tag Žiadne tagy, Buďte prvý, kto otaguje tento záznam!

Buďte prvý, kto okomentuje tento záznam!