The deposition of thin films of cadmium zinc sulfide Cd1−x Zn x S at 250 °C from spin-coated xanthato complexes: a potential route to window layers for photovoltaic cells

Thin films of Cd1−xZnxS (CZS) were prepared by a novel spin coating/melt method from cadmium ethylxanthato [Cd(C2H5OCS2)2] and zinc ethylxanthato [Zn(C2H5OCS2)2] in x ratios of 0–0.15 and of 1. A solution of the precursor(s) in THF was spin coated onto a glass substrate and then heated at 250 °C for...

Celý popis

Uloženo v:

Podrobná bibliografie
Vydáno v:	Journal of materials science Ročník 53; číslo 6; s. 4360 - 4370
Hlavní autoři:	Bakly, Ali A. K., Spencer, Ben F., O’Brien, Paul
Médium:	Journal Article
Jazyk:	angličtina
Vydáno:	New York Springer Nature B.V 01.03.2018
Témata:	Cadmium coatings Electrical resistivity Emission analysis energy-dispersive X-ray analysis glass Glass substrates Inductively coupled plasma Materials science melting nitrogen Photovoltaic cells Precursors Raman spectroscopy scanning electron microscopy Solar cells solar energy Spectrum analysis Spin coating Thickness Thin films ultraviolet-visible spectroscopy X ray photoelectron spectroscopy Zinc Zinc sulfide
ISSN:	0022-2461, 1573-4803
On-line přístup:	Získat plný text
Tagy:	Přidat tag Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!

Buďte první, kdo okomentuje tento záznam!