A Simple Sonochemical Synthesis of Nanosized ZnO from Zinc Acetate and Sodium Hydroxide

An efficient sonochemical route for synthesis of nano sized zinc oxide is reported. The method employs zinc acetate and sodium hydroxide as precursors with isopropyl alcohol as a solvent. As prepared powders were characterized by XRD, SEM and FTIR. These show that the resulting powder is composed of...

Celý popis

Uloženo v:
Podrobná bibliografie
Vydáno v:Journal of Nano- and Electronic Physics Ročník 10; číslo 5; s. 5023 - 5023-4
Hlavní autoři: Zakirov, M. I., Semen'ko, M. P., Korotchenkov, O. A.
Médium: Journal Article
Jazyk:angličtina
Vydáno: Sumy Ukraine Sumy State University, Journal of Nano - and Electronic Physics 2018
Témata:
Caustic soda
Crystallites
Isopropanol
Metal hydroxides
Sodium hydroxide
Synthesis
Wurtzite
Zinc acetate
Zinc oxide
Zinc oxides
ISSN:2077-6772, 2306-4277
On-line přístup:Získat plný text
Tagy: Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
Popis
Shrnutí:An efficient sonochemical route for synthesis of nano sized zinc oxide is reported. The method employs zinc acetate and sodium hydroxide as precursors with isopropyl alcohol as a solvent. As prepared powders were characterized by XRD, SEM and FTIR. These show that the resulting powder is composed of multi-domain crystallites of ZnO wurtzite, zincite and Zn(OH)2. The XRD-measured coherent domain size varies from about 20 to 30 nm, whereas SEM exhibits 200 nm crystallites. The wurtzite phase is found to dominate at sonication times smaller than 30 min. It is also found that the powders produced sonochemically exhibit smaller and narrower size-distributed particles compared to that in hydrothermally prepared powders.
Bibliografie:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:2077-6772
2306-4277
DOI:10.21272/jnep.10(5).05023