Salt Recovery from the Hot Treated Aluminium Melting Dross Residue

In the aluminium industry, the large amount of dross – a by-product of scrap melting – is usually further processed at high temperature re-melting to reclaim the high metallic content entrapped in material. The residue of the hot dross treatment is mainly composed of oxides, and chloride salts from...

Full description

Saved in:
Bibliographic Details
Published in:Hungarian materials and chemical sciences and engineering (Online) Vol. 47; no. 1; pp. 128 - 137
Main Authors: Hegedüs, Balázs, Nagy, Gábor, Kékesi, Tamás
Format: Journal Article
Language:English
Published: Miskolc University of Miskolc 05.11.2023
Subjects:
Aluminum
Crystallization
Dross
Efficiency
Energy consumption
Heat
High temperature
Latent heat
Leaching
Melting
Metal industry
Potassium chloride
Residues
Room temperature
ISSN:3004-0000, 3004-0817
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:In the aluminium industry, the large amount of dross – a by-product of scrap melting – is usually further processed at high temperature re-melting to reclaim the high metallic content entrapped in material. The residue of the hot dross treatment is mainly composed of oxides, and chloride salts from the flux added during the thermo-mechanical process. The major NaCl and KCl components of the added salt are removed by a technically simple leaching process, however, the brine must be treated to remove the dissolved chlorides. We have investigated the energy requirement and efficiency of the evaporation procedure with a simple vessel of insulated walls and submerged heater. The specific heat capacity of the examined NaCl/KCl saturated solution of 2 : 1 mass ratio was determined as ~3155 J/kgK and the latent heat as 1538 J/kgK. The heat efficiency obtained with the system at room temperature initially was found to approach a 97% level as stable conditions were reached. The crystallized NaCl/KCl salt mixture – with possible modifications of it composition – can be recycled to the furnace.
Bibliography:ObjectType-Article-1
SourceType-Scholarly Journals-1
ObjectType-Feature-2
content type line 14
ISSN:3004-0000
3004-0817
DOI:10.32974/mse.2022.013