Electroceramics for High-Energy Density Capacitors: Current Status and Future Perspectives
Materials exhibiting high energy/power density are currently needed to meet the growing demand of portable electronics, electric vehicles and large-scale energy storage devices. The highest energy densities are achieved for fuel cells, batteries, and supercapacitors, but conventional dielectric capa...
Uloženo v:
| Vydáno v: | Chemical reviews Ročník 121; číslo 10; s. 6124 |
|---|---|
| Hlavní autoři: | , , , , , , , , , |
| Médium: | Journal Article |
| Jazyk: | angličtina |
| Vydáno: |
United States
26.05.2021
|
| ISSN: | 1520-6890, 1520-6890 |
| On-line přístup: | Zjistit podrobnosti o přístupu |
| Tagy: |
Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
|
| Abstract | Materials exhibiting high energy/power density are currently needed to meet the growing demand of portable electronics, electric vehicles and large-scale energy storage devices. The highest energy densities are achieved for fuel cells, batteries, and supercapacitors, but conventional dielectric capacitors are receiving increased attention for pulsed power applications due to their high power density and their fast charge-discharge speed. The key to high energy density in dielectric capacitors is a large maximum but small remanent (zero in the case of linear dielectrics) polarization and a high electric breakdown strength. Polymer dielectric capacitors offer high power/energy density for applications at room temperature, but above 100 °C they are unreliable and suffer from dielectric breakdown. For high-temperature applications, therefore, dielectric ceramics are the only feasible alternative. Lead-based ceramics such as La-doped lead zirconate titanate exhibit good energy storage properties, but their toxicity raises concern over their use in consumer applications, where capacitors are exclusively lead free. Lead-free compositions with superior power density are thus required. In this paper, we introduce the fundamental principles of energy storage in dielectrics. We discuss key factors to improve energy storage properties such as the control of local structure, phase assemblage, dielectric layer thickness, microstructure, conductivity, and electrical homogeneity through the choice of base systems, dopants, and alloying additions, followed by a comprehensive review of the state-of-the-art. Finally, we comment on the future requirements for new materials in high power/energy density capacitor applications. |
|---|---|
| AbstractList | Materials exhibiting high energy/power density are currently needed to meet the growing demand of portable electronics, electric vehicles and large-scale energy storage devices. The highest energy densities are achieved for fuel cells, batteries, and supercapacitors, but conventional dielectric capacitors are receiving increased attention for pulsed power applications due to their high power density and their fast charge-discharge speed. The key to high energy density in dielectric capacitors is a large maximum but small remanent (zero in the case of linear dielectrics) polarization and a high electric breakdown strength. Polymer dielectric capacitors offer high power/energy density for applications at room temperature, but above 100 °C they are unreliable and suffer from dielectric breakdown. For high-temperature applications, therefore, dielectric ceramics are the only feasible alternative. Lead-based ceramics such as La-doped lead zirconate titanate exhibit good energy storage properties, but their toxicity raises concern over their use in consumer applications, where capacitors are exclusively lead free. Lead-free compositions with superior power density are thus required. In this paper, we introduce the fundamental principles of energy storage in dielectrics. We discuss key factors to improve energy storage properties such as the control of local structure, phase assemblage, dielectric layer thickness, microstructure, conductivity, and electrical homogeneity through the choice of base systems, dopants, and alloying additions, followed by a comprehensive review of the state-of-the-art. Finally, we comment on the future requirements for new materials in high power/energy density capacitor applications. Materials exhibiting high energy/power density are currently needed to meet the growing demand of portable electronics, electric vehicles and large-scale energy storage devices. The highest energy densities are achieved for fuel cells, batteries, and supercapacitors, but conventional dielectric capacitors are receiving increased attention for pulsed power applications due to their high power density and their fast charge-discharge speed. The key to high energy density in dielectric capacitors is a large maximum but small remanent (zero in the case of linear dielectrics) polarization and a high electric breakdown strength. Polymer dielectric capacitors offer high power/energy density for applications at room temperature, but above 100 °C they are unreliable and suffer from dielectric breakdown. For high-temperature applications, therefore, dielectric ceramics are the only feasible alternative. Lead-based ceramics such as La-doped lead zirconate titanate exhibit good energy storage properties, but their toxicity raises concern over their use in consumer applications, where capacitors are exclusively lead free. Lead-free compositions with superior power density are thus required. In this paper, we introduce the fundamental principles of energy storage in dielectrics. We discuss key factors to improve energy storage properties such as the control of local structure, phase assemblage, dielectric layer thickness, microstructure, conductivity, and electrical homogeneity through the choice of base systems, dopants, and alloying additions, followed by a comprehensive review of the state-of-the-art. Finally, we comment on the future requirements for new materials in high power/energy density capacitor applications.Materials exhibiting high energy/power density are currently needed to meet the growing demand of portable electronics, electric vehicles and large-scale energy storage devices. The highest energy densities are achieved for fuel cells, batteries, and supercapacitors, but conventional dielectric capacitors are receiving increased attention for pulsed power applications due to their high power density and their fast charge-discharge speed. The key to high energy density in dielectric capacitors is a large maximum but small remanent (zero in the case of linear dielectrics) polarization and a high electric breakdown strength. Polymer dielectric capacitors offer high power/energy density for applications at room temperature, but above 100 °C they are unreliable and suffer from dielectric breakdown. For high-temperature applications, therefore, dielectric ceramics are the only feasible alternative. Lead-based ceramics such as La-doped lead zirconate titanate exhibit good energy storage properties, but their toxicity raises concern over their use in consumer applications, where capacitors are exclusively lead free. Lead-free compositions with superior power density are thus required. In this paper, we introduce the fundamental principles of energy storage in dielectrics. We discuss key factors to improve energy storage properties such as the control of local structure, phase assemblage, dielectric layer thickness, microstructure, conductivity, and electrical homogeneity through the choice of base systems, dopants, and alloying additions, followed by a comprehensive review of the state-of-the-art. Finally, we comment on the future requirements for new materials in high power/energy density capacitor applications. |
| Author | Ji, Hongfen Wang, Dawei Wang, Ge Li, Linhao Feteira, Antonio Lu, Zhilun Li, Yong Reaney, Ian M Zhang, Shujun Zhou, Di |
| Author_xml | – sequence: 1 givenname: Ge orcidid: 0000-0003-1842-8067 surname: Wang fullname: Wang, Ge organization: Department of Materials Science and Engineering, University of Sheffield, Sheffield S1 3JD, U.K – sequence: 2 givenname: Zhilun surname: Lu fullname: Lu, Zhilun organization: The Henry Royce Institute, Sir Robert Hadfield Building, Sheffield S1 3JD, U.K – sequence: 3 givenname: Yong surname: Li fullname: Li, Yong organization: Inner Mongolia Key Laboratory of Ferroelectric-related New Energy Materials and Devices, School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou 014010, China – sequence: 4 givenname: Linhao surname: Li fullname: Li, Linhao organization: Department of Materials Science and Engineering, University of Sheffield, Sheffield S1 3JD, U.K – sequence: 5 givenname: Hongfen surname: Ji fullname: Ji, Hongfen organization: Laboratory of Thin Film Techniques and Optical Test, Xi'an Technological University, Xi'an 710032, China – sequence: 6 givenname: Antonio surname: Feteira fullname: Feteira, Antonio organization: Christian Doppler Laboratory for Advanced Ferroic Oxides, Sheffield Hallam University, Sheffield S1 1WB, U.K – sequence: 7 givenname: Di orcidid: 0000-0001-7411-4658 surname: Zhou fullname: Zhou, Di organization: Electronic Materials Research Lab, Key Lab of Education Ministry/International Center for Dielectric Research, School of Electronic and Information Engineering, Xi'an Jiaotong University, Xi'an 710049, China – sequence: 8 givenname: Dawei orcidid: 0000-0001-6957-2494 surname: Wang fullname: Wang, Dawei organization: Shenzhen Institute of Advanced Electronic Materials, Shenzhen Institute of Advanced Technology, Chinese Academy of Sciences, Shenzhen 518055, China – sequence: 9 givenname: Shujun orcidid: 0000-0001-6139-6887 surname: Zhang fullname: Zhang, Shujun organization: Institute for Superconducting and Electronic Materials, Australian Institute for Innovative Materials, University of Wollongong, Wollongong, NSW 2500, Australia – sequence: 10 givenname: Ian M orcidid: 0000-0003-3893-6544 surname: Reaney fullname: Reaney, Ian M organization: Department of Materials Science and Engineering, University of Sheffield, Sheffield S1 3JD, U.K |
| BackLink | https://www.ncbi.nlm.nih.gov/pubmed/33909415$$D View this record in MEDLINE/PubMed |
| BookMark | eNpNkEtLw0AUhQep2If-AkFm6Sb1ziSTdNxJbK1QUFA3bsJk5qaN5OU8Cv33Fqzg5pyz-PgWZ0pGXd8hIdcM5gw4u1PazfUOW4v7OWhgPE3OyIQJDlG6kDD6t8dk6twXAAjBswsyjmMJMmFiQj6XDWpve41WtbV2tOotXdfbXbTs0G4P9BE7V_sDzdWgdO176-5pHqzFztM3r3xwVHWGroIPFukrWjcchfUe3SU5r1Tj8OrUM_KxWr7n62jz8vScP2wiJTLuI6WQl7rMQDImQcfalIppZpLYLJjmnGdCZRxklZbMZLJSZZwIiI0pWaUxY3xGbn-9g-2_AzpftLXT2DSqwz64ggsmF3CM9IjenNBQtmiKwdatsofi7w_-A6k_Z5I |
| CitedBy_id | crossref_primary_10_1016_j_jallcom_2022_165019 crossref_primary_10_1016_j_ceramint_2022_06_148 crossref_primary_10_1016_j_ceramint_2024_03_057 crossref_primary_10_1016_j_ceramint_2024_03_299 crossref_primary_10_1016_j_mseb_2025_118712 crossref_primary_10_1016_j_powtec_2025_121557 crossref_primary_10_1038_s41598_025_03386_w crossref_primary_10_1016_j_cej_2023_145705 crossref_primary_10_1007_s40820_023_01290_4 crossref_primary_10_1016_j_jeurceramsoc_2023_08_017 crossref_primary_10_1038_s41467_025_62658_1 crossref_primary_10_1063_5_0217327 crossref_primary_10_1111_jace_19611 crossref_primary_10_1016_j_matchemphys_2023_127717 crossref_primary_10_1002_adma_202313285 crossref_primary_10_1016_j_ceramint_2025_04_375 crossref_primary_10_1038_s41467_025_59226_y crossref_primary_10_1111_jace_19610 crossref_primary_10_1016_j_cej_2025_162844 crossref_primary_10_1016_j_materresbull_2024_113232 crossref_primary_10_1016_j_apmt_2024_102488 crossref_primary_10_1021_jacs_3c13405 crossref_primary_10_70322_htm_2025_10010 crossref_primary_10_1016_j_ceramint_2024_09_115 crossref_primary_10_1016_j_ceramint_2024_11_289 crossref_primary_10_1021_acsami_5c03588 crossref_primary_10_1002_adfm_202503798 crossref_primary_10_26599_JAC_2024_9220833 crossref_primary_10_1016_j_actamat_2024_120079 crossref_primary_10_1063_5_0134282 crossref_primary_10_1016_j_ceramint_2024_03_286 crossref_primary_10_1111_jace_19868 crossref_primary_10_1016_j_jallcom_2025_183771 crossref_primary_10_1002_advs_202502916 crossref_primary_10_1002_advs_202203926 crossref_primary_10_1007_s10853_023_08771_2 crossref_primary_10_1016_j_ceramint_2023_06_208 crossref_primary_10_1016_j_jallcom_2025_181126 crossref_primary_10_1016_j_mtchem_2021_100583 crossref_primary_10_1111_jace_18745 crossref_primary_10_1016_j_ceramint_2023_02_190 crossref_primary_10_1007_s10854_024_11938_5 crossref_primary_10_1016_j_compositesb_2021_109493 crossref_primary_10_1016_j_ceramint_2023_07_247 crossref_primary_10_1016_j_jpowsour_2024_235846 crossref_primary_10_1016_j_ceramint_2022_05_118 crossref_primary_10_1016_j_ceramint_2023_07_004 crossref_primary_10_1016_j_est_2024_114992 crossref_primary_10_26599_JAC_2024_9220859 crossref_primary_10_1002_adfm_202502204 crossref_primary_10_3390_cryst15080736 crossref_primary_10_1016_j_ceramint_2025_05_396 crossref_primary_10_1002_aelm_202300187 crossref_primary_10_1063_5_0226027 crossref_primary_10_1111_jace_19600 crossref_primary_10_4150_KPMI_2023_30_6_509 crossref_primary_10_1007_s10854_025_15451_1 crossref_primary_10_1016_j_ceramint_2024_02_237 crossref_primary_10_1016_j_jeurceramsoc_2023_09_053 crossref_primary_10_1016_j_cej_2023_147097 crossref_primary_10_1002_aelm_202200503 crossref_primary_10_3390_molecules29133187 crossref_primary_10_1016_j_jeurceramsoc_2021_12_032 crossref_primary_10_1016_j_jmst_2024_05_046 crossref_primary_10_1016_j_matchemphys_2022_126542 crossref_primary_10_1002_asia_202500602 crossref_primary_10_1016_j_physb_2024_416385 crossref_primary_10_1016_j_tsf_2024_140266 crossref_primary_10_1021_acsaenm_5c00566 crossref_primary_10_1016_j_ceramint_2024_10_446 crossref_primary_10_1002_adfm_202305251 crossref_primary_10_1016_j_jmrt_2025_08_195 crossref_primary_10_1016_j_est_2024_112755 crossref_primary_10_1063_5_0066002 crossref_primary_10_1016_j_est_2024_112752 crossref_primary_10_1016_j_jallcom_2024_176519 crossref_primary_10_1002_smll_202106515 crossref_primary_10_1016_j_jallcom_2024_176753 crossref_primary_10_1016_j_mtcomm_2024_109581 crossref_primary_10_1021_acsami_5c06895 crossref_primary_10_1016_j_matchemphys_2024_130119 crossref_primary_10_1016_j_ceramint_2022_12_104 crossref_primary_10_1016_j_nanoen_2024_109791 crossref_primary_10_1016_j_cej_2023_142862 crossref_primary_10_1016_j_mattod_2023_07_023 crossref_primary_10_1016_j_jeurceramsoc_2024_02_040 crossref_primary_10_1016_j_jpowsour_2025_237061 crossref_primary_10_1016_j_ceramint_2021_10_217 crossref_primary_10_1111_jace_18977 crossref_primary_10_1016_j_ceramint_2025_04_194 crossref_primary_10_1016_j_cej_2025_161727 crossref_primary_10_1002_aesr_202100191 crossref_primary_10_1007_s10854_024_12233_z crossref_primary_10_3390_ma15124360 crossref_primary_10_1016_j_actamat_2023_118730 crossref_primary_10_1016_j_cej_2025_167263 crossref_primary_10_1007_s10853_024_10174_w crossref_primary_10_1016_j_ceramint_2024_03_078 crossref_primary_10_1016_j_scriptamat_2023_115387 crossref_primary_10_1002_eom2_12331 crossref_primary_10_1016_j_chemphys_2024_112203 crossref_primary_10_1002_adfm_202516412 crossref_primary_10_1016_j_ceramint_2024_10_427 crossref_primary_10_1016_j_jeurceramsoc_2024_02_011 crossref_primary_10_1016_j_jeurceramsoc_2024_02_012 crossref_primary_10_1007_s42823_023_00604_1 crossref_primary_10_1016_j_jcis_2024_07_158 crossref_primary_10_1063_5_0237117 crossref_primary_10_1016_j_ceramint_2022_07_129 crossref_primary_10_1007_s10854_025_14729_8 crossref_primary_10_1016_j_jeurceramsoc_2021_12_028 crossref_primary_10_1021_jacs_3c06912 crossref_primary_10_1002_adem_202201847 crossref_primary_10_1007_s40820_024_01363_y crossref_primary_10_1016_j_egyr_2022_03_130 crossref_primary_10_1007_s41779_024_01142_3 crossref_primary_10_1016_j_mseb_2023_117033 crossref_primary_10_1038_s41563_022_01274_6 crossref_primary_10_1039_D4QI02126F crossref_primary_10_1039_D2MH00912A crossref_primary_10_1002_smll_202106302 crossref_primary_10_1016_j_ceramint_2024_02_036 crossref_primary_10_1016_j_jallcom_2023_173199 crossref_primary_10_3390_polym15102315 crossref_primary_10_1007_s42452_025_06996_1 crossref_primary_10_1016_j_ceramint_2022_04_139 crossref_primary_10_1016_j_matchemphys_2022_127032 crossref_primary_10_1002_advs_202405730 crossref_primary_10_1002_ange_202500516 crossref_primary_10_1016_j_jallcom_2023_171144 crossref_primary_10_1016_j_ceramint_2025_02_369 crossref_primary_10_1016_j_ceramint_2024_07_103 crossref_primary_10_1016_j_actamat_2022_117734 crossref_primary_10_1063_5_0051853 crossref_primary_10_1007_s10853_025_10778_w crossref_primary_10_1007_s40145_022_0613_3 crossref_primary_10_1016_j_ceramint_2022_12_149 crossref_primary_10_1016_j_matdes_2022_111447 crossref_primary_10_1039_D4RA06275B crossref_primary_10_1007_s10971_023_06150_6 crossref_primary_10_1016_j_ceramint_2024_08_142 crossref_primary_10_1002_sus2_174 crossref_primary_10_3390_cryst15010026 crossref_primary_10_1016_j_ceramint_2023_07_058 crossref_primary_10_1016_j_jpowsour_2024_235698 crossref_primary_10_1016_j_ceramint_2022_12_151 crossref_primary_10_1016_j_ceramint_2024_11_438 crossref_primary_10_1016_j_jeurceramsoc_2023_07_042 crossref_primary_10_1016_j_jpowsour_2025_236845 crossref_primary_10_1016_j_ceramint_2025_03_191 crossref_primary_10_1002_advs_202104569 crossref_primary_10_3390_cryst14080732 crossref_primary_10_1016_j_est_2025_118321 crossref_primary_10_1016_j_ceramint_2024_08_171 crossref_primary_10_1016_j_cej_2021_133584 crossref_primary_10_1016_j_ceramint_2023_05_239 crossref_primary_10_1016_j_est_2023_109044 crossref_primary_10_1016_j_jallcom_2024_174710 crossref_primary_10_1016_j_jpowsour_2024_235203 crossref_primary_10_1080_27660400_2025_2506975 crossref_primary_10_2109_jcersj2_25007 crossref_primary_10_3390_ma15145057 crossref_primary_10_1016_j_cej_2025_163751 crossref_primary_10_1063_5_0102088 crossref_primary_10_1016_j_ceramint_2025_09_010 crossref_primary_10_1016_j_jeurceramsoc_2023_06_037 crossref_primary_10_1016_j_ceramint_2024_01_278 crossref_primary_10_1021_jacs_5c07213 crossref_primary_10_1016_j_cej_2024_153421 crossref_primary_10_1038_s41467_025_56443_3 crossref_primary_10_1016_j_cej_2021_133579 crossref_primary_10_1002_admi_202201257 crossref_primary_10_1016_j_jallcom_2025_180210 crossref_primary_10_1021_acsaem_5c01616 crossref_primary_10_1002_ange_202416291 crossref_primary_10_1016_j_ceramint_2022_11_131 crossref_primary_10_1016_j_ceramint_2022_06_184 crossref_primary_10_3390_ma16114144 crossref_primary_10_1002_adma_202204356 crossref_primary_10_1002_smll_202306803 crossref_primary_10_1016_j_jeurceramsoc_2024_116917 crossref_primary_10_1016_j_apsusc_2025_163697 crossref_primary_10_1016_j_est_2023_108374 crossref_primary_10_1016_j_ceramint_2024_09_392 crossref_primary_10_1007_s12598_023_02271_7 crossref_primary_10_1039_D2RA03685A crossref_primary_10_1002_smll_202503713 crossref_primary_10_1016_j_cej_2023_141376 crossref_primary_10_1016_j_actamat_2024_120278 crossref_primary_10_1016_j_jeurceramsoc_2025_117282 crossref_primary_10_1016_j_ceramint_2023_08_087 crossref_primary_10_1002_smll_202303768 crossref_primary_10_1016_j_jallcom_2024_174724 crossref_primary_10_1002_aenm_202203961 crossref_primary_10_1007_s10853_021_06704_5 crossref_primary_10_1007_s12598_022_02176_x crossref_primary_10_1016_j_ceramint_2024_07_316 crossref_primary_10_1016_j_apenergy_2022_119730 crossref_primary_10_1016_j_cclet_2025_111436 crossref_primary_10_1016_j_cej_2022_136925 crossref_primary_10_1016_j_cej_2024_149154 crossref_primary_10_1016_j_jeurceramsoc_2023_07_002 crossref_primary_10_1016_j_ceramint_2025_08_417 crossref_primary_10_1002_aenm_202203925 crossref_primary_10_1016_j_ceramint_2023_08_296 crossref_primary_10_1016_j_nanoen_2025_110891 crossref_primary_10_1016_j_ceramint_2023_09_098 crossref_primary_10_1016_j_jallcom_2023_172255 crossref_primary_10_1016_j_cej_2024_152786 crossref_primary_10_1002_adfm_202108496 crossref_primary_10_3390_molecules26226952 crossref_primary_10_1002_adma_202312856 crossref_primary_10_1016_j_ceramint_2023_07_043 crossref_primary_10_1007_s10854_023_10642_0 crossref_primary_10_1016_j_mtener_2022_101208 crossref_primary_10_1016_j_est_2025_117200 crossref_primary_10_1016_j_jallcom_2025_180242 crossref_primary_10_1016_j_jmst_2022_10_053 crossref_primary_10_1016_j_jtice_2023_105290 crossref_primary_10_1007_s10854_023_11605_1 crossref_primary_10_1016_j_cej_2024_155803 crossref_primary_10_1021_acsami_5c04646 crossref_primary_10_1016_j_jeurceramsoc_2023_07_020 crossref_primary_10_1063_5_0191645 crossref_primary_10_1016_j_scriptamat_2023_115888 crossref_primary_10_1021_acsaem_5c00961 crossref_primary_10_1007_s12598_022_02225_5 crossref_primary_10_1016_j_mtphys_2024_101418 crossref_primary_10_1016_j_jallcom_2023_169575 crossref_primary_10_1016_j_jics_2025_101637 crossref_primary_10_1016_j_cej_2022_137367 crossref_primary_10_1016_j_ceramint_2022_02_248 crossref_primary_10_1016_j_apenergy_2024_123479 crossref_primary_10_1016_j_ceramint_2024_04_413 crossref_primary_10_1039_D5EE02541A crossref_primary_10_1016_j_ceramint_2022_09_356 crossref_primary_10_1016_j_ceramint_2024_05_455 crossref_primary_10_1016_j_ceramint_2024_04_416 crossref_primary_10_1016_j_ceramint_2024_07_062 crossref_primary_10_1016_j_jallcom_2025_178611 crossref_primary_10_1016_j_ceramint_2023_05_173 crossref_primary_10_1016_j_jallcom_2024_175067 crossref_primary_10_1111_jace_19050 crossref_primary_10_5940_jcrsj_67_30 crossref_primary_10_1021_jacs_3c09805 crossref_primary_10_1016_j_jallcom_2022_164851 crossref_primary_10_1016_j_materresbull_2023_112664 crossref_primary_10_1016_j_ceramint_2022_08_300 crossref_primary_10_1016_j_cclet_2023_108598 crossref_primary_10_1111_jace_20045 crossref_primary_10_1016_j_cclet_2024_110728 crossref_primary_10_3390_nano13050899 crossref_primary_10_1016_j_jeurceramsoc_2022_12_064 crossref_primary_10_1016_j_solidstatesciences_2022_106906 crossref_primary_10_1016_j_jallcom_2021_163212 crossref_primary_10_1007_s10854_023_10009_5 crossref_primary_10_1016_j_cej_2023_147664 crossref_primary_10_1016_j_actamat_2024_120522 crossref_primary_10_1016_j_jpcs_2024_112099 crossref_primary_10_1021_acsami_5c06072 crossref_primary_10_1063_5_0100614 crossref_primary_10_1016_j_ensm_2025_104082 crossref_primary_10_1063_5_0237948 crossref_primary_10_1111_jace_20277 crossref_primary_10_1007_s10971_024_06485_8 crossref_primary_10_1007_s10854_022_09351_x crossref_primary_10_1002_smll_202302346 crossref_primary_10_1007_s10854_021_07404_1 crossref_primary_10_1111_jace_19270 crossref_primary_10_1016_j_ceramint_2023_12_023 crossref_primary_10_1016_j_susmat_2024_e01172 crossref_primary_10_1016_j_cej_2024_157986 crossref_primary_10_1002_adfm_202516297 crossref_primary_10_1016_j_jmat_2025_101065 crossref_primary_10_1111_ijac_15069 crossref_primary_10_1111_jace_18194 crossref_primary_10_1007_s12598_021_01869_z crossref_primary_10_3390_cryst13040649 crossref_primary_10_1016_j_jeurceramsoc_2023_06_048 crossref_primary_10_1039_D3EE01545A crossref_primary_10_1016_j_scriptamat_2023_115602 crossref_primary_10_1049_hve2_12438 crossref_primary_10_1016_j_ceramint_2025_08_118 crossref_primary_10_1111_jace_19017 crossref_primary_10_1016_j_jeurceramsoc_2023_06_045 crossref_primary_10_3390_cryst14040296 crossref_primary_10_1016_j_cej_2024_150091 crossref_primary_10_1016_j_ceramint_2025_01_098 crossref_primary_10_1007_s40974_023_00286_5 crossref_primary_10_1038_s41467_022_30821_7 crossref_primary_10_1016_j_mtener_2022_101185 crossref_primary_10_1016_j_cej_2025_163459 crossref_primary_10_1038_s41467_024_53287_1 crossref_primary_10_1016_j_jallcom_2025_182903 crossref_primary_10_1016_j_jmat_2024_100980 crossref_primary_10_1016_j_ceramint_2022_03_261 crossref_primary_10_1016_j_jeurceramsoc_2025_117326 crossref_primary_10_1007_s10854_022_08958_4 crossref_primary_10_1002_adma_202207580 crossref_primary_10_1016_j_jeurceramsoc_2023_07_081 crossref_primary_10_1038_s41467_025_57228_4 crossref_primary_10_1116_6_0004172 crossref_primary_10_1016_j_jeurceramsoc_2023_04_024 crossref_primary_10_1016_j_cej_2025_166739 crossref_primary_10_1111_jace_19029 crossref_primary_10_1016_j_coco_2024_102238 crossref_primary_10_1016_j_pmatsci_2023_101231 crossref_primary_10_1016_j_ceramint_2025_08_364 crossref_primary_10_1016_j_cej_2024_154695 crossref_primary_10_1016_j_mtener_2022_101193 crossref_primary_10_1016_j_ceramint_2024_12_353 crossref_primary_10_1111_jace_19266 crossref_primary_10_1016_j_cej_2021_133999 crossref_primary_10_1002_adfm_202414393 crossref_primary_10_1016_j_cej_2024_154442 crossref_primary_10_1002_aelm_202201141 crossref_primary_10_1016_j_jmat_2025_101097 crossref_primary_10_1016_j_mtchem_2025_103013 crossref_primary_10_1016_j_jallcom_2022_164859 crossref_primary_10_1016_j_fuel_2023_128122 crossref_primary_10_1016_j_jeurceramsoc_2023_06_073 crossref_primary_10_1007_s10854_022_09000_3 crossref_primary_10_1016_j_mtphys_2024_101420 crossref_primary_10_1016_j_ceramint_2025_08_385 crossref_primary_10_1063_5_0235963 crossref_primary_10_1016_j_nxsust_2024_100036 crossref_primary_10_1016_j_matpr_2022_06_542 crossref_primary_10_1016_j_jeurceramsoc_2022_08_010 crossref_primary_10_1002_adfm_202406148 crossref_primary_10_1016_j_jeurceramsoc_2025_117539 crossref_primary_10_1016_j_ceramint_2023_10_005 crossref_primary_10_1016_j_jallcom_2022_168124 crossref_primary_10_1021_acsami_5c08878 crossref_primary_10_1063_5_0144267 crossref_primary_10_1007_s12598_025_03411_x crossref_primary_10_1016_j_ceramint_2024_03_201 crossref_primary_10_1016_j_jeurceramsoc_2022_08_020 crossref_primary_10_1016_j_jeurceramsoc_2023_03_021 crossref_primary_10_1016_j_jeurceramsoc_2022_08_021 crossref_primary_10_1016_j_cej_2025_168318 crossref_primary_10_1016_j_jallcom_2023_169723 crossref_primary_10_1016_j_ceramint_2022_08_148 crossref_primary_10_1007_s12633_025_03251_5 crossref_primary_10_1002_adma_202502788 crossref_primary_10_1016_j_ceramint_2024_12_151 crossref_primary_10_1016_j_jallcom_2024_176548 crossref_primary_10_1007_s10853_024_09953_2 crossref_primary_10_1016_j_ceramint_2021_09_006 crossref_primary_10_1063_5_0145369 crossref_primary_10_1002_adma_202108772 crossref_primary_10_1007_s10832_022_00283_w crossref_primary_10_1021_jacs_3c08903 crossref_primary_10_1103_gfl2_bsjk crossref_primary_10_1016_j_surfin_2024_104632 crossref_primary_10_1111_jace_18589 crossref_primary_10_1016_j_physb_2025_417493 crossref_primary_10_1088_1361_665X_ad5d33 crossref_primary_10_1016_j_jmst_2023_08_031 crossref_primary_10_1007_s10854_023_11161_8 crossref_primary_10_1016_j_cap_2023_12_008 crossref_primary_10_1038_s41586_022_05671_4 crossref_primary_10_1063_5_0102882 crossref_primary_10_1002_anie_202416291 crossref_primary_10_1002_admt_202202044 crossref_primary_10_1002_adfm_202409446 crossref_primary_10_1016_j_nanoen_2023_108458 crossref_primary_10_1016_j_ceramint_2024_05_278 crossref_primary_10_1016_j_molstruc_2023_136352 crossref_primary_10_1016_j_ensm_2025_104257 crossref_primary_10_1016_j_jeurceramsoc_2025_117786 crossref_primary_10_20517_microstructures_2024_131 crossref_primary_10_1016_j_jeurceramsoc_2025_117785 crossref_primary_10_1002_smll_202206840 crossref_primary_10_1016_j_ceramint_2023_11_089 crossref_primary_10_1002_app_57113 crossref_primary_10_1016_j_ssc_2025_115843 crossref_primary_10_1016_j_mseb_2025_118640 crossref_primary_10_1016_j_surfin_2024_105737 crossref_primary_10_1007_s10965_021_02877_4 crossref_primary_10_1016_j_jallcom_2023_170962 crossref_primary_10_1016_j_jallcom_2024_176569 crossref_primary_10_1126_science_adt2703 crossref_primary_10_1016_j_ceramint_2023_11_079 crossref_primary_10_1016_j_cej_2024_149947 crossref_primary_10_1016_j_eurpolymj_2023_112543 crossref_primary_10_1016_j_ceramint_2024_02_203 crossref_primary_10_3390_batteries10120447 crossref_primary_10_1111_jace_20651 crossref_primary_10_1016_j_ceramint_2023_10_057 crossref_primary_10_1002_adfm_202305524 crossref_primary_10_1016_j_ceramint_2025_06_190 crossref_primary_10_1039_D2MH01530G crossref_primary_10_1111_jace_19410 crossref_primary_10_1111_jace_20657 crossref_primary_10_1016_j_mtcomm_2024_111159 crossref_primary_10_1049_nde2_12069 crossref_primary_10_1111_jace_20413 crossref_primary_10_1016_j_jallcom_2022_163721 crossref_primary_10_1007_s42835_025_02156_y crossref_primary_10_1016_j_mseb_2022_115773 crossref_primary_10_1111_jace_19426 crossref_primary_10_1007_s12598_024_03051_7 crossref_primary_10_1016_j_est_2024_114786 crossref_primary_10_1111_jace_70065 crossref_primary_10_1038_s41467_025_61250_x crossref_primary_10_1016_j_jallcom_2023_170786 crossref_primary_10_1002_est2_642 crossref_primary_10_1016_j_jallcom_2024_177433 crossref_primary_10_1016_j_jpowsour_2024_236062 crossref_primary_10_1016_j_ceramint_2023_03_156 crossref_primary_10_1016_j_jallcom_2024_176372 crossref_primary_10_1016_j_mtphys_2022_100821 crossref_primary_10_1002_adfm_202213804 crossref_primary_10_26599_JAC_2023_9220821 crossref_primary_10_1016_j_cej_2022_138432 crossref_primary_10_1016_j_cej_2022_137105 crossref_primary_10_1088_1742_6596_2680_1_012007 crossref_primary_10_1016_j_cej_2024_154047 crossref_primary_10_1007_s10854_023_11655_5 crossref_primary_10_1016_j_ceramint_2021_07_004 crossref_primary_10_1016_j_matlet_2022_133576 crossref_primary_10_1016_j_revmat_2025_100006 crossref_primary_10_1038_s41467_025_56195_0 crossref_primary_10_1002_adfm_202411954 crossref_primary_10_1038_s41467_024_53661_z crossref_primary_10_1002_smll_202504695 crossref_primary_10_3390_jcs7070282 crossref_primary_10_1016_j_actamat_2022_118286 crossref_primary_10_1016_j_ceramint_2025_05_111 crossref_primary_10_1002_smll_202202203 crossref_primary_10_1007_s12274_024_6704_4 crossref_primary_10_1016_j_jallcom_2023_169300 crossref_primary_10_1016_j_ceramint_2025_06_161 crossref_primary_10_1016_j_jnoncrysol_2023_122788 crossref_primary_10_1016_j_jcis_2024_01_075 crossref_primary_10_1016_j_physb_2023_414652 crossref_primary_10_1016_j_ceramint_2024_11_179 crossref_primary_10_1016_j_nanoen_2022_107276 crossref_primary_10_1039_D4RA08061K crossref_primary_10_1002_smll_202309796 crossref_primary_10_1016_j_jece_2024_113784 crossref_primary_10_1016_j_nanoen_2023_108275 crossref_primary_10_1002_admt_202101530 crossref_primary_10_1002_advs_202409814 crossref_primary_10_1016_j_cej_2023_144973 crossref_primary_10_1016_j_jeurceramsoc_2023_01_025 crossref_primary_10_1016_j_ceramint_2022_06_260 crossref_primary_10_1016_j_pmatsci_2024_101385 crossref_primary_10_1007_s10853_022_07350_1 crossref_primary_10_1016_j_jmst_2023_10_026 crossref_primary_10_1016_j_ceramint_2024_01_329 crossref_primary_10_1016_j_ceramint_2024_02_368 crossref_primary_10_1016_j_actamat_2023_118826 crossref_primary_10_3390_ma15175881 crossref_primary_10_1016_j_ceramint_2023_10_097 crossref_primary_10_1038_s41467_025_63041_w crossref_primary_10_1016_j_ijsolstr_2025_113392 crossref_primary_10_1134_S0036024424701747 crossref_primary_10_26599_JAC_2024_9220939 crossref_primary_10_1002_smll_202206662 crossref_primary_10_1016_j_jeurceramsoc_2023_01_036 crossref_primary_10_1016_j_ceramint_2022_06_277 crossref_primary_10_1038_s41467_025_60685_6 crossref_primary_10_1016_j_cej_2021_133277 crossref_primary_10_3390_cryst13020295 crossref_primary_10_1016_j_jeurceramsoc_2023_10_056 crossref_primary_10_1111_ijac_70004 crossref_primary_10_1016_j_jeurceramsoc_2023_01_005 crossref_primary_10_1016_j_ceramint_2024_01_304 crossref_primary_10_1016_j_jeurceramsoc_2025_117832 crossref_primary_10_1111_ijac_14535 crossref_primary_10_1016_j_cej_2023_141449 crossref_primary_10_1016_j_ceramint_2025_06_088 crossref_primary_10_1016_j_ceramint_2023_02_070 crossref_primary_10_1007_s42773_022_00176_9 crossref_primary_10_1016_j_cej_2022_135762 crossref_primary_10_1016_j_ceramint_2024_04_199 crossref_primary_10_1016_j_ceramint_2024_02_101 crossref_primary_10_1016_j_ceramint_2025_06_091 crossref_primary_10_1016_j_jeurceramsoc_2022_07_030 crossref_primary_10_1002_aenm_202400821 crossref_primary_10_1016_j_cej_2022_135523 crossref_primary_10_1002_adma_202406219 crossref_primary_10_1016_j_cej_2024_152624 crossref_primary_10_1016_j_jcis_2021_11_137 crossref_primary_10_1038_s41467_025_56605_3 crossref_primary_10_1063_5_0145299 crossref_primary_10_1021_jacs_4c10907 crossref_primary_10_1016_j_apmt_2025_102895 crossref_primary_10_1002_advs_202105368 crossref_primary_10_1007_s10853_024_09482_y crossref_primary_10_1039_D5TC00384A crossref_primary_10_1016_j_ceramint_2024_02_118 crossref_primary_10_1016_j_scriptamat_2025_116751 crossref_primary_10_26599_JAC_2024_9220965 crossref_primary_10_1016_j_actamat_2025_121511 crossref_primary_10_1111_jace_18849 crossref_primary_10_3390_ma16247634 crossref_primary_10_1016_j_compositesa_2022_107019 crossref_primary_10_1016_j_jallcom_2025_183442 crossref_primary_10_1002_pssa_202400306 crossref_primary_10_1111_ijac_14360 crossref_primary_10_1002_adfm_202409344 crossref_primary_10_1016_j_cej_2022_135789 crossref_primary_10_1016_j_cej_2025_160500 crossref_primary_10_1039_D5MH00261C crossref_primary_10_1038_s41598_024_68420_9 crossref_primary_10_1007_s43538_025_00473_4 crossref_primary_10_1016_j_ceramint_2022_07_265 crossref_primary_10_1016_j_scriptamat_2023_115295 crossref_primary_10_1016_j_nanoen_2023_108477 crossref_primary_10_1016_j_mtsust_2022_100310 crossref_primary_10_1016_j_ceramint_2024_01_376 crossref_primary_10_1039_D4SC05437G crossref_primary_10_1002_anie_202500516 crossref_primary_10_1007_s10971_024_06433_6 crossref_primary_10_1016_j_flatc_2022_100467 crossref_primary_10_1021_acsapm_5c00118 crossref_primary_10_1109_JESTIE_2024_3385709 crossref_primary_10_1016_j_jeurceramsoc_2022_07_029 crossref_primary_10_1016_j_jeurceramsoc_2022_07_025 crossref_primary_10_3390_ma15072506 crossref_primary_10_1016_j_jeurceramsoc_2023_01_049 crossref_primary_10_1111_jace_19919 crossref_primary_10_1016_j_jmat_2023_09_009 crossref_primary_10_1038_s41560_023_01300_0 crossref_primary_10_1039_D5TA04848F crossref_primary_10_1063_5_0226576 crossref_primary_10_1016_j_ceramint_2024_10_310 crossref_primary_10_1016_j_cej_2022_139921 crossref_primary_10_1016_j_compositesb_2023_111189 crossref_primary_10_1016_j_cej_2024_152823 crossref_primary_10_1016_j_cej_2025_167352 crossref_primary_10_1016_j_jmat_2023_09_004 crossref_primary_10_1016_j_jpcs_2021_110513 crossref_primary_10_1007_s10854_024_13470_y crossref_primary_10_1016_j_cej_2022_140924 crossref_primary_10_3390_ma18122809 crossref_primary_10_1016_j_ceramint_2021_12_151 crossref_primary_10_1016_j_ceramint_2022_07_011 crossref_primary_10_1002_apxr_202300006 crossref_primary_10_1007_s40843_022_2412_2 crossref_primary_10_1021_acsaem_5c01536 crossref_primary_10_1016_j_actamat_2023_119071 crossref_primary_10_1002_crat_202200147 crossref_primary_10_1007_s00339_023_06758_z crossref_primary_10_1016_j_cej_2021_133441 crossref_primary_10_1016_j_ceramint_2024_07_224 crossref_primary_10_1016_j_cej_2021_133447 crossref_primary_10_1002_advs_202300320 crossref_primary_10_1007_s10854_022_08455_8 crossref_primary_10_1039_D4EE03705G crossref_primary_10_3390_ma17205044 crossref_primary_10_1039_D2CC01951E crossref_primary_10_1016_j_jpowsour_2024_234495 crossref_primary_10_1002_advs_202400174 crossref_primary_10_1016_j_jeurceramsoc_2022_06_077 crossref_primary_10_1039_D3MH00078H crossref_primary_10_1016_j_est_2024_112841 crossref_primary_10_1016_j_actamat_2025_121380 crossref_primary_10_1007_s10854_025_15428_0 crossref_primary_10_1016_j_materresbull_2023_112392 crossref_primary_10_1021_acsaelm_5c00215 crossref_primary_10_1016_j_ceramint_2023_05_107 crossref_primary_10_1016_j_actamat_2024_120109 crossref_primary_10_1016_j_cej_2025_161485 crossref_primary_10_1016_j_cej_2025_164723 crossref_primary_10_1002_adfm_202210050 crossref_primary_10_1002_slct_202400425 crossref_primary_10_1016_j_materresbull_2023_112157 crossref_primary_10_1016_j_rser_2024_114624 crossref_primary_10_1016_j_ssi_2024_116647 crossref_primary_10_1016_j_jeurceramsoc_2024_116815 crossref_primary_10_1016_j_matchemphys_2025_131032 crossref_primary_10_1016_j_progpolymsci_2025_101957 crossref_primary_10_1016_j_mtphys_2023_101208 crossref_primary_10_1016_j_jeurceramsoc_2022_12_007 crossref_primary_10_1016_j_ceramint_2025_08_349 crossref_primary_10_1016_j_jpowsour_2024_234475 crossref_primary_10_1002_aenm_202403926 crossref_primary_10_1038_s41578_024_00702_0 crossref_primary_10_1007_s10854_022_07731_x crossref_primary_10_3390_nano12050730 crossref_primary_10_1016_j_jeurceramsoc_2024_116824 crossref_primary_10_1016_j_jallcom_2025_182737 crossref_primary_10_1111_ijac_14373 crossref_primary_10_1016_j_scriptamat_2024_115966 crossref_primary_10_1016_j_scriptamat_2024_115968 crossref_primary_10_1002_smll_202404581 crossref_primary_10_1016_j_actamat_2022_118505 crossref_primary_10_1016_j_jallcom_2024_174610 crossref_primary_10_1016_j_apmt_2024_102326 crossref_primary_10_1007_s41779_024_01087_7 crossref_primary_10_1063_5_0142200 crossref_primary_10_1039_D5QI00216H crossref_primary_10_1002_adfm_202507692 crossref_primary_10_1021_jacs_3c02811 crossref_primary_10_1016_j_jeurceramsoc_2022_06_031 crossref_primary_10_1016_j_est_2024_111711 crossref_primary_10_1007_s11270_023_06784_w crossref_primary_10_1016_j_ceramint_2024_05_407 crossref_primary_10_1007_s10854_025_14665_7 crossref_primary_10_1016_j_cej_2023_141490 crossref_primary_10_1016_j_ceramint_2024_09_025 crossref_primary_10_1016_j_ceramint_2024_06_402 crossref_primary_10_1016_j_progpolymsci_2024_101870 crossref_primary_10_1007_s43207_024_00450_5 crossref_primary_10_1016_j_ceramint_2021_11_197 crossref_primary_10_3390_cryst15020160 crossref_primary_10_1016_j_ceramint_2023_08_170 crossref_primary_10_1016_j_cej_2024_150476 crossref_primary_10_1016_j_jeurceramsoc_2025_117197 crossref_primary_10_1007_s10832_023_00343_9 crossref_primary_10_1016_j_jpowsour_2024_234677 crossref_primary_10_1002_adma_202310559 crossref_primary_10_1080_00150193_2023_2201775 crossref_primary_10_1002_er_7897 crossref_primary_10_1016_j_jallcom_2023_172373 crossref_primary_10_1016_j_jallcom_2023_171044 crossref_primary_10_1002_adfm_202111776 crossref_primary_10_1063_5_0143758 crossref_primary_10_1016_j_jallcom_2022_164236 crossref_primary_10_1002_adma_202410088 crossref_primary_10_1016_j_ceramint_2024_06_415 crossref_primary_10_1016_j_jallcom_2025_183878 crossref_primary_10_1016_j_matchemphys_2023_127629 crossref_primary_10_1016_j_ceramint_2025_08_300 crossref_primary_10_1002_adma_202205787 crossref_primary_10_1016_j_cej_2021_132165 crossref_primary_10_1016_j_jallcom_2023_172147 crossref_primary_10_1021_acsami_5c05854 crossref_primary_10_1038_s41467_024_50252_w crossref_primary_10_1016_j_jeurceramsoc_2022_11_002 crossref_primary_10_1002_advs_202414380 crossref_primary_10_1016_j_ceramint_2022_12_294 crossref_primary_10_1016_j_ceramint_2024_07_211 crossref_primary_10_1016_j_ceramint_2023_07_153 crossref_primary_10_1007_s13391_023_00434_3 crossref_primary_10_1002_adma_202403400 crossref_primary_10_3390_app12052591 crossref_primary_10_1016_j_jeurceramsoc_2022_03_037 crossref_primary_10_1134_S0036029525700454 crossref_primary_10_1007_s10854_024_12864_2 crossref_primary_10_1007_s10854_024_13970_x crossref_primary_10_1016_j_nanoen_2024_110065 crossref_primary_10_1007_s10854_024_13761_4 crossref_primary_10_1016_j_mtcomm_2024_110815 crossref_primary_10_1016_j_jeurceramsoc_2022_02_005 crossref_primary_10_1016_j_electacta_2024_145381 crossref_primary_10_1016_j_ceramint_2025_09_083 crossref_primary_10_1016_j_nanoen_2022_107577 crossref_primary_10_1016_j_ceramint_2024_07_195 crossref_primary_10_1016_j_ceramint_2021_08_171 crossref_primary_10_1016_j_mtchem_2022_101353 crossref_primary_10_1111_jace_20155 crossref_primary_10_1111_jace_20156 crossref_primary_10_1016_j_cej_2024_154369 crossref_primary_10_26599_JAC_2025_9221088 crossref_primary_10_1016_j_actamat_2023_119135 crossref_primary_10_1016_j_ceramint_2023_11_363 crossref_primary_10_1016_j_ceramint_2022_09_208 crossref_primary_10_1016_j_cej_2021_131684 crossref_primary_10_1016_j_vacuum_2024_113130 crossref_primary_10_26599_JAC_2023_9220752 crossref_primary_10_1016_j_colsurfa_2022_130450 crossref_primary_10_1021_jacs_2c12200 crossref_primary_10_1021_jacs_4c02868 crossref_primary_10_3389_fenrg_2021_807300 crossref_primary_10_1002_inf2_12488 crossref_primary_10_1038_s41598_024_81758_4 crossref_primary_10_1557_s43578_022_00640_z crossref_primary_10_1016_j_jallcom_2023_170205 crossref_primary_10_1016_j_ceramint_2024_05_302 crossref_primary_10_1021_acsami_5c09213 crossref_primary_10_1016_j_ceramint_2022_11_092 crossref_primary_10_1016_j_jeurceramsoc_2023_12_036 crossref_primary_10_1007_s00339_024_08162_7 crossref_primary_10_26599_JAC_2025_9221063 crossref_primary_10_1016_j_cej_2022_139222 crossref_primary_10_3390_electronics12061297 crossref_primary_10_1016_j_ceramint_2022_04_177 crossref_primary_10_1016_j_ceramint_2023_10_322 crossref_primary_10_1007_s40820_023_01036_2 crossref_primary_10_1016_j_joule_2022_12_010 crossref_primary_10_1016_j_cej_2024_158940 crossref_primary_10_1016_j_ceramint_2022_10_297 crossref_primary_10_1016_j_cej_2023_142070 crossref_primary_10_1016_j_cej_2023_142071 crossref_primary_10_1016_j_ceramint_2025_09_033 crossref_primary_10_1016_j_cej_2023_146673 crossref_primary_10_1016_j_jallcom_2023_172671 crossref_primary_10_1002_admi_202201824 crossref_primary_10_1063_5_0190404 crossref_primary_10_1016_j_cej_2023_146426 crossref_primary_10_1016_j_actamat_2025_121184 crossref_primary_10_1016_j_ceramint_2023_12_166 crossref_primary_10_1016_j_polymer_2024_127001 crossref_primary_10_3390_cryst12020141 crossref_primary_10_1016_j_mtcomm_2024_108702 crossref_primary_10_1016_j_mtener_2022_101078 crossref_primary_10_1016_j_jallcom_2025_179878 crossref_primary_10_1002_pssa_202200240 crossref_primary_10_1007_s10854_025_15772_1 crossref_primary_10_1016_j_mssp_2024_108458 crossref_primary_10_1016_j_jallcom_2021_163139 crossref_primary_10_1016_j_jeurceramsoc_2024_117151 crossref_primary_10_1016_j_jeurceramsoc_2025_117239 crossref_primary_10_1016_j_jeurceramsoc_2022_04_057 crossref_primary_10_1016_j_cej_2024_151046 crossref_primary_10_1016_j_cej_2024_151043 crossref_primary_10_1016_j_ceramint_2025_07_009 crossref_primary_10_1063_5_0094247 crossref_primary_10_1016_j_ceramint_2025_07_248 crossref_primary_10_1002_adfm_202302995 crossref_primary_10_1016_j_ceramint_2022_02_106 crossref_primary_10_1016_j_jmst_2025_02_058 crossref_primary_10_1016_j_scriptamat_2022_115194 crossref_primary_10_1016_j_ceramint_2025_07_242 crossref_primary_10_1038_s41467_024_50831_x crossref_primary_10_1016_j_cej_2023_147974 crossref_primary_10_1016_j_diamond_2025_112557 crossref_primary_10_1016_j_ceramint_2025_06_436 crossref_primary_10_1016_j_ceramint_2023_06_073 crossref_primary_10_1016_j_ceramint_2025_08_270 crossref_primary_10_20517_jmi_2024_97 crossref_primary_10_1016_j_ceramint_2023_05_049 crossref_primary_10_1007_s10971_024_06375_z crossref_primary_10_1002_smll_202205624 crossref_primary_10_1016_j_ceramint_2022_08_272 crossref_primary_10_1149_1945_7111_ae0552 crossref_primary_10_1007_s10854_023_10252_w crossref_primary_10_1016_j_mseb_2025_118551 crossref_primary_10_1016_j_cej_2022_135462 crossref_primary_10_1016_j_ceramint_2024_12_259 crossref_primary_10_1016_j_ceramint_2024_12_018 crossref_primary_10_1007_s41918_024_00214_z crossref_primary_10_1016_j_ceramint_2022_07_229 crossref_primary_10_1111_ijac_14962 crossref_primary_10_1016_j_ceramint_2023_09_116 crossref_primary_10_1007_s11837_024_07077_1 crossref_primary_10_1111_jace_19349 crossref_primary_10_3390_ceramics7020047 crossref_primary_10_1016_j_ceramint_2023_10_143 crossref_primary_10_1038_s41467_025_56181_6 crossref_primary_10_1063_5_0229392 crossref_primary_10_1007_s10854_023_10043_3 crossref_primary_10_1016_j_ceramint_2024_12_276 crossref_primary_10_3390_nano13101587 crossref_primary_10_1039_D5DT01380A crossref_primary_10_1103_PhysRevApplied_19_054064 crossref_primary_10_1016_j_ceramint_2025_06_249 crossref_primary_10_1002_adfm_202200848 crossref_primary_10_1111_jace_19556 crossref_primary_10_1016_j_cej_2022_136330 crossref_primary_10_1016_j_ceramint_2022_09_053 crossref_primary_10_1126_science_adn8721 crossref_primary_10_1088_1402_4896_ad32c4 crossref_primary_10_1016_j_scriptamat_2024_116287 crossref_primary_10_1016_j_cej_2025_167790 crossref_primary_10_54227_mlab_20220057 crossref_primary_10_3390_ceramics7030068 crossref_primary_10_1002_ajoc_202400719 crossref_primary_10_1016_j_ceramint_2023_03_087 crossref_primary_10_3390_catal13040779 crossref_primary_10_3390_ceramics7030065 crossref_primary_10_1016_j_jmat_2025_101107 crossref_primary_10_1111_jace_18239 crossref_primary_10_1016_j_ceramint_2025_05_439 crossref_primary_10_1111_jace_19329 crossref_primary_10_1007_s10854_025_15467_7 crossref_primary_10_1016_j_cej_2022_135497 crossref_primary_10_1016_j_ceramint_2023_10_167 crossref_primary_10_1063_5_0086042 crossref_primary_10_1016_j_jallcom_2024_175358 crossref_primary_10_1016_j_cap_2023_08_012 crossref_primary_10_1016_j_solidstatesciences_2024_107616 crossref_primary_10_1038_s41467_024_51058_6 crossref_primary_10_1016_j_ceramint_2024_09_403 crossref_primary_10_1007_s12274_024_6793_0 crossref_primary_10_1016_j_actamat_2025_120943 crossref_primary_10_1016_j_mtchem_2022_100898 crossref_primary_10_1002_adfm_202502853 crossref_primary_10_26599_JAC_2023_9220728 crossref_primary_10_1016_j_mtcomm_2025_112885 crossref_primary_10_1038_s41467_025_59081_x crossref_primary_10_1002_smll_202306486 crossref_primary_10_1007_s12598_023_02452_4 crossref_primary_10_1016_j_jallcom_2021_163556 crossref_primary_10_1016_j_mtchem_2024_102384 crossref_primary_10_1007_s00396_024_05240_3 crossref_primary_10_1016_j_mtphys_2023_101054 crossref_primary_10_1111_jace_19776 crossref_primary_10_1021_acssuschemeng_4c07306 crossref_primary_10_1002_pc_27052 crossref_primary_10_1063_5_0288959 crossref_primary_10_1021_acsnano_5c02357 crossref_primary_10_1038_s41467_025_56194_1 crossref_primary_10_1111_jace_19774 crossref_primary_10_1016_j_cej_2025_166440 crossref_primary_10_1063_5_0148785 crossref_primary_10_1016_j_actamat_2025_120931 crossref_primary_10_1016_j_ceramint_2024_03_368 crossref_primary_10_1007_s10832_025_00422_z crossref_primary_10_1016_j_ceramint_2025_03_427 crossref_primary_10_1002_adfm_202513315 crossref_primary_10_1016_j_cej_2024_156112 crossref_primary_10_1111_jace_20520 crossref_primary_10_1016_j_jallcom_2024_177559 crossref_primary_10_1016_j_jallcom_2024_177558 crossref_primary_10_1007_s40145_022_0566_6 crossref_primary_10_1111_jace_18455 crossref_primary_10_1002_smll_202306236 crossref_primary_10_1016_j_jallcom_2024_177556 crossref_primary_10_1063_5_0135242 crossref_primary_10_1002_smll_202202575 crossref_primary_10_1039_D5TA05149E crossref_primary_10_3390_mi16010007 crossref_primary_10_1016_j_diamond_2023_110161 crossref_primary_10_1016_j_electacta_2025_145845 crossref_primary_10_1039_D5TA05234C crossref_primary_10_1088_1361_6463_acbbd9 crossref_primary_10_1002_smtd_202300830 crossref_primary_10_1016_j_cej_2025_164008 crossref_primary_10_1002_adfm_202301027 crossref_primary_10_1016_j_cej_2025_164009 crossref_primary_10_1002_smll_202400686 crossref_primary_10_1002_advs_202409113 crossref_primary_10_1016_j_ceramint_2021_08_133 crossref_primary_10_1002_adma_202419563 crossref_primary_10_1016_j_jechem_2025_07_047 crossref_primary_10_1002_adma_202420566 crossref_primary_10_1016_j_est_2024_112010 crossref_primary_10_1038_s41467_025_62335_3 crossref_primary_10_1038_s41467_024_49107_1 crossref_primary_10_1016_j_cej_2025_166433 crossref_primary_10_26599_JAC_2023_9220713 crossref_primary_10_1002_aelm_202200793 crossref_primary_10_1016_j_cej_2025_166438 crossref_primary_10_1007_s10854_022_08317_3 crossref_primary_10_1080_15583724_2022_2129680 crossref_primary_10_1016_j_est_2024_113599 crossref_primary_10_1016_j_ceramint_2022_08_208 crossref_primary_10_1016_j_inoche_2024_113137 crossref_primary_10_1016_j_jpcs_2022_111176 crossref_primary_10_1016_j_cej_2021_133812 crossref_primary_10_1016_j_nanoen_2023_108544 crossref_primary_10_1016_j_cej_2023_147572 crossref_primary_10_26599_JAC_2023_9220708 |
| ContentType | Journal Article |
| DBID | NPM 7X8 |
| DOI | 10.1021/acs.chemrev.0c01264 |
| DatabaseName | PubMed MEDLINE - Academic |
| DatabaseTitle | PubMed MEDLINE - Academic |
| DatabaseTitleList | PubMed MEDLINE - Academic |
| Database_xml | – sequence: 1 dbid: NPM name: PubMed url: http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed sourceTypes: Index Database – sequence: 2 dbid: 7X8 name: MEDLINE - Academic url: https://search.proquest.com/medline sourceTypes: Aggregation Database |
| DeliveryMethod | no_fulltext_linktorsrc |
| Discipline | Chemistry |
| EISSN | 1520-6890 |
| ExternalDocumentID | 33909415 |
| Genre | Journal Article |
| GroupedDBID | --- -DZ -~X .DC .K2 29B 4.4 53G 55A 5GY 5RE 5VS 6J9 7~N 85S AABXI AAHBH ABBLG ABJNI ABLBI ABMVS ABPPZ ABQRX ABUCX ACGFO ACGFS ACGOD ACIWK ACJ ACNCT ACS ADHLV AEESW AENEX AFEFF AFXLT AGXLV AHGAQ ALMA_UNASSIGNED_HOLDINGS AQSVZ BAANH BKOMP CS3 CUPRZ D0L DU5 EBS ED~ F5P GGK GNL IH9 IHE JG~ LG6 NPM P2P PQQKQ ROL RWL TAE TN5 UI2 UKR UPT VF5 VG9 W1F WH7 XSW YZZ ~02 7X8 ABUFD |
| ID | FETCH-LOGICAL-a572t-aae2bcb7091190c3cdba1c1d43d81c22275a7209f6b1d79fab34503ddb1fce712 |
| IEDL.DBID | 7X8 |
| ISICitedReferencesCount | 1023 |
| ISICitedReferencesURI | http://www.webofscience.com/api/gateway?GWVersion=2&SrcApp=Summon&SrcAuth=ProQuest&DestLinkType=CitingArticles&DestApp=WOS_CPL&KeyUT=000657259900008&url=https%3A%2F%2Fcvtisr.summon.serialssolutions.com%2F%23%21%2Fsearch%3Fho%3Df%26include.ft.matches%3Dt%26l%3Dnull%26q%3D |
| ISSN | 1520-6890 |
| IngestDate | Sun Nov 09 13:07:34 EST 2025 Mon Jul 21 05:41:28 EDT 2025 |
| IsDoiOpenAccess | false |
| IsOpenAccess | true |
| IsPeerReviewed | true |
| IsScholarly | true |
| Issue | 10 |
| Language | English |
| LinkModel | DirectLink |
| MergedId | FETCHMERGED-LOGICAL-a572t-aae2bcb7091190c3cdba1c1d43d81c22275a7209f6b1d79fab34503ddb1fce712 |
| Notes | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
| ORCID | 0000-0001-6139-6887 0000-0003-1842-8067 0000-0001-7411-4658 0000-0001-6957-2494 0000-0003-3893-6544 |
| OpenAccessLink | https://doi.org/10.1021/acs.chemrev.0c01264 |
| PMID | 33909415 |
| PQID | 2519805196 |
| PQPubID | 23479 |
| ParticipantIDs | proquest_miscellaneous_2519805196 pubmed_primary_33909415 |
| PublicationCentury | 2000 |
| PublicationDate | 2021-05-26 |
| PublicationDateYYYYMMDD | 2021-05-26 |
| PublicationDate_xml | – month: 05 year: 2021 text: 2021-05-26 day: 26 |
| PublicationDecade | 2020 |
| PublicationPlace | United States |
| PublicationPlace_xml | – name: United States |
| PublicationTitle | Chemical reviews |
| PublicationTitleAlternate | Chem Rev |
| PublicationYear | 2021 |
| SSID | ssj0005527 |
| Score | 2.7458296 |
| SecondaryResourceType | review_article |
| Snippet | Materials exhibiting high energy/power density are currently needed to meet the growing demand of portable electronics, electric vehicles and large-scale... |
| SourceID | proquest pubmed |
| SourceType | Aggregation Database Index Database |
| StartPage | 6124 |
| Title | Electroceramics for High-Energy Density Capacitors: Current Status and Future Perspectives |
| URI | https://www.ncbi.nlm.nih.gov/pubmed/33909415 https://www.proquest.com/docview/2519805196 |
| Volume | 121 |
| WOSCitedRecordID | wos000657259900008&url=https%3A%2F%2Fcvtisr.summon.serialssolutions.com%2F%23%21%2Fsearch%3Fho%3Df%26include.ft.matches%3Dt%26l%3Dnull%26q%3D |
| hasFullText | |
| inHoldings | 1 |
| isFullTextHit | |
| isPrint | |
| link | http://cvtisr.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwpZ3PS8MwFMeDOkEv_v79gwhew5JmWVovInPDi2MHheFlJC8perBTOwX_e99rO3YSBC-9Fdo0fe-T5L3vl7FLBVGaGEDkIFPRcdoKH0wUluhfQehKSCuzCTscpuNxNmo23MqmrHIeE6tAHaZAe-Rt6rBMiTe612_vglyj6HS1sdBYZi2NKEMlXXa8UAs3tWUrpihcIqWZnKsOJartAD_pc3wloxcJGKVJcuA3xqxyzWDzv0-5xTYayuQ39bTYZkux2GFrvbm52y576tf2NxA_yJC-5MiunGo-RL9qBuS3VNg---Y9TKbwQpY8V7zRcuIEqJ8ld0Xgg0qShI8WLZvlHnsc9B96d6KxWRDO2GQmnIuJB2-RHJAOQEPwToEKHR1SBdQra5xNZJZ3vQo2y53XHSN1CF7lEK1K9tlKMS3iIePIngaM9M6A6nidY6hF_rQ5Mgxk1mVH7GI-bBN8YTqbcEWcfpaTxcAdsYN67Cdvtd7GROsMF6HKHP_h7hO2nlDViaTavVPWyvEnjmdsFb5mL-XHeTU_8Doc3f8AN6PHIw |
| linkProvider | ProQuest |
| openUrl | ctx_ver=Z39.88-2004&ctx_enc=info%3Aofi%2Fenc%3AUTF-8&rfr_id=info%3Asid%2Fsummon.serialssolutions.com&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Ajournal&rft.genre=article&rft.atitle=Electroceramics+for+High-Energy+Density+Capacitors%3A+Current+Status+and+Future+Perspectives&rft.jtitle=Chemical+reviews&rft.au=Wang%2C+Ge&rft.au=Lu%2C+Zhilun&rft.au=Li%2C+Yong&rft.au=Li%2C+Linhao&rft.date=2021-05-26&rft.eissn=1520-6890&rft_id=info:doi/10.1021%2Facs.chemrev.0c01264&rft_id=info%3Apmid%2F33909415&rft_id=info%3Apmid%2F33909415&rft.externalDocID=33909415 |
| thumbnail_l | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/lc.gif&issn=1520-6890&client=summon |
| thumbnail_m | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/mc.gif&issn=1520-6890&client=summon |
| thumbnail_s | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/sc.gif&issn=1520-6890&client=summon |