Microporous Metal-Organic Frameworks for Adsorptive Separation of C5-C6 Alkane Isomers
The separation of alkane isomers, particularly C5-C6 alkanes, is of paramount importance in the petrochemical industry to achieve high quality gasoline. Upon catalytic isomerization reactions, less branched alkanes (with lower octane number) need to be separated from their more branched isomers (wit...
Uloženo v:
| Vydáno v: | Accounts of chemical research Ročník 52; číslo 7; s. 1968 |
|---|---|
| Hlavní autoři: | , |
| Médium: | Journal Article |
| Jazyk: | angličtina |
| Vydáno: |
United States
16.07.2019
|
| ISSN: | 1520-4898, 1520-4898 |
| On-line přístup: | Zjistit podrobnosti o přístupu |
| Tagy: |
Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
|
| Abstract | The separation of alkane isomers, particularly C5-C6 alkanes, is of paramount importance in the petrochemical industry to achieve high quality gasoline. Upon catalytic isomerization reactions, less branched alkanes (with lower octane number) need to be separated from their more branched isomers (with higher octane number) in order to improve the octane rating of gasoline. To reduce the high energy input associated with distillations, the primary separation technique currently used in industry, adsorptive separation by porous solids has been proposed. For example, zeolite 5A has been used as the adsorbent material for adsorptive separation of linear alkanes from their branched isomers, as a supplement technology to distillations. However, due to the limited number of zeolite structures and the lack of porosity tenability in these compounds, the task has not been fully fulfilled by using zeolites. Metal-organic frameworks (MOFs), in light of their structural diversity and high tunability in terms of surface area, pore size, and pore shape, offer new opportunities for resolving industrially relevant separation of alkanes through selective adsorption. This Account summarizes recent development of microporous MOFs for the separation of alkanes, with an emphasis on C5-C6 alkane isomers, including early examples of alkane separation by MOFs, as well as the latest advancement on tailor-made microporous MOFs for size sieving of C5-C6 alkane isomers. The limitation of zeolite 5A as a sorbent material for the separation of C5-C6 alkane isomers lies in its relatively low adsorption capacity. In addition, it is not capable of separating branched alkanes, which is a crucial step for further improving the octane rating of gasoline. The high porosity and tunable pore size and pore shape of MOFs may afford them higher adsorption capacity and selectivity when used for alkane separation. MOFs with pore size slightly larger than the kinetic diameter of branched alkanes can effectively separate alkane isomers through thermodynamically controlled separation, as seen in the case of Fe
(bdp)
(bdp
= 1,4-benzenedipyrazolate). This MOF is capable of separating a mixture of hexane isomers by the degrees of branching, with higher adsorption capacity than zeolites under similar conditions but with relatively low selectivity. One effective strategy for obtaining MOFs with optimal pore size and pore shape for highly selective adsorption is to make use of reticular chemistry and precise ligand design. By applying topologically directed design strategy and precisely controlling the pore structure or ligand functionality, we have successfully synthesized a series of highly robust MOFs built on tetratopic carboxylate linkers that demonstrate high performance for the separation of C5-C6 alkane isomers. Zr-bptc (bptc
= 3,3',5,5'-biphenyltetracarboxylate) adsorbs linear alkanes only and excludes all branched isomers. This size-exclusion mechanism is very similar to that of zeolite 5A. Yet, Zr-bptc has a significantly enhanced adsorption capacity for
-hexane, 70% higher than that of zeolite 5A under identical conditions. Zr-abtc (abtc
= 3,3',5,5'-azobenzenetetracarboxylate) is capable of discriminating all three C6 alkane isomers via a thermodynamically controlled process, yielding a high separation factor for monobranched over dibranched isomers. MOFs with flexible framework may exhibit unexpected but desired adsorption properties. Ca(H
tcpb) (tcpb
= 1,2,4,5-tetrakis(4-carboxyphenyl)-benzene) can fully separate binary or ternary mixtures of C5-C6 alkane isomers into pure form through selective molecular sieving as a result of its temperature- and adsorbate-dependent framework flexibility. The intriguing structural properties and exceptional tunability of these MOFs make them promising candidates for industrial implementation of adsorptive separation of alkane isomers. |
|---|---|
| AbstractList | The separation of alkane isomers, particularly C5-C6 alkanes, is of paramount importance in the petrochemical industry to achieve high quality gasoline. Upon catalytic isomerization reactions, less branched alkanes (with lower octane number) need to be separated from their more branched isomers (with higher octane number) in order to improve the octane rating of gasoline. To reduce the high energy input associated with distillations, the primary separation technique currently used in industry, adsorptive separation by porous solids has been proposed. For example, zeolite 5A has been used as the adsorbent material for adsorptive separation of linear alkanes from their branched isomers, as a supplement technology to distillations. However, due to the limited number of zeolite structures and the lack of porosity tenability in these compounds, the task has not been fully fulfilled by using zeolites. Metal-organic frameworks (MOFs), in light of their structural diversity and high tunability in terms of surface area, pore size, and pore shape, offer new opportunities for resolving industrially relevant separation of alkanes through selective adsorption. This Account summarizes recent development of microporous MOFs for the separation of alkanes, with an emphasis on C5-C6 alkane isomers, including early examples of alkane separation by MOFs, as well as the latest advancement on tailor-made microporous MOFs for size sieving of C5-C6 alkane isomers. The limitation of zeolite 5A as a sorbent material for the separation of C5-C6 alkane isomers lies in its relatively low adsorption capacity. In addition, it is not capable of separating branched alkanes, which is a crucial step for further improving the octane rating of gasoline. The high porosity and tunable pore size and pore shape of MOFs may afford them higher adsorption capacity and selectivity when used for alkane separation. MOFs with pore size slightly larger than the kinetic diameter of branched alkanes can effectively separate alkane isomers through thermodynamically controlled separation, as seen in the case of Fe2(bdp)3 (bdp2- = 1,4-benzenedipyrazolate). This MOF is capable of separating a mixture of hexane isomers by the degrees of branching, with higher adsorption capacity than zeolites under similar conditions but with relatively low selectivity. One effective strategy for obtaining MOFs with optimal pore size and pore shape for highly selective adsorption is to make use of reticular chemistry and precise ligand design. By applying topologically directed design strategy and precisely controlling the pore structure or ligand functionality, we have successfully synthesized a series of highly robust MOFs built on tetratopic carboxylate linkers that demonstrate high performance for the separation of C5-C6 alkane isomers. Zr-bptc (bptc4-= 3,3',5,5'-biphenyltetracarboxylate) adsorbs linear alkanes only and excludes all branched isomers. This size-exclusion mechanism is very similar to that of zeolite 5A. Yet, Zr-bptc has a significantly enhanced adsorption capacity for n-hexane, 70% higher than that of zeolite 5A under identical conditions. Zr-abtc (abtc4- = 3,3',5,5'-azobenzenetetracarboxylate) is capable of discriminating all three C6 alkane isomers via a thermodynamically controlled process, yielding a high separation factor for monobranched over dibranched isomers. MOFs with flexible framework may exhibit unexpected but desired adsorption properties. Ca(H2tcpb) (tcpb4- = 1,2,4,5-tetrakis(4-carboxyphenyl)-benzene) can fully separate binary or ternary mixtures of C5-C6 alkane isomers into pure form through selective molecular sieving as a result of its temperature- and adsorbate-dependent framework flexibility. The intriguing structural properties and exceptional tunability of these MOFs make them promising candidates for industrial implementation of adsorptive separation of alkane isomers.The separation of alkane isomers, particularly C5-C6 alkanes, is of paramount importance in the petrochemical industry to achieve high quality gasoline. Upon catalytic isomerization reactions, less branched alkanes (with lower octane number) need to be separated from their more branched isomers (with higher octane number) in order to improve the octane rating of gasoline. To reduce the high energy input associated with distillations, the primary separation technique currently used in industry, adsorptive separation by porous solids has been proposed. For example, zeolite 5A has been used as the adsorbent material for adsorptive separation of linear alkanes from their branched isomers, as a supplement technology to distillations. However, due to the limited number of zeolite structures and the lack of porosity tenability in these compounds, the task has not been fully fulfilled by using zeolites. Metal-organic frameworks (MOFs), in light of their structural diversity and high tunability in terms of surface area, pore size, and pore shape, offer new opportunities for resolving industrially relevant separation of alkanes through selective adsorption. This Account summarizes recent development of microporous MOFs for the separation of alkanes, with an emphasis on C5-C6 alkane isomers, including early examples of alkane separation by MOFs, as well as the latest advancement on tailor-made microporous MOFs for size sieving of C5-C6 alkane isomers. The limitation of zeolite 5A as a sorbent material for the separation of C5-C6 alkane isomers lies in its relatively low adsorption capacity. In addition, it is not capable of separating branched alkanes, which is a crucial step for further improving the octane rating of gasoline. The high porosity and tunable pore size and pore shape of MOFs may afford them higher adsorption capacity and selectivity when used for alkane separation. MOFs with pore size slightly larger than the kinetic diameter of branched alkanes can effectively separate alkane isomers through thermodynamically controlled separation, as seen in the case of Fe2(bdp)3 (bdp2- = 1,4-benzenedipyrazolate). This MOF is capable of separating a mixture of hexane isomers by the degrees of branching, with higher adsorption capacity than zeolites under similar conditions but with relatively low selectivity. One effective strategy for obtaining MOFs with optimal pore size and pore shape for highly selective adsorption is to make use of reticular chemistry and precise ligand design. By applying topologically directed design strategy and precisely controlling the pore structure or ligand functionality, we have successfully synthesized a series of highly robust MOFs built on tetratopic carboxylate linkers that demonstrate high performance for the separation of C5-C6 alkane isomers. Zr-bptc (bptc4-= 3,3',5,5'-biphenyltetracarboxylate) adsorbs linear alkanes only and excludes all branched isomers. This size-exclusion mechanism is very similar to that of zeolite 5A. Yet, Zr-bptc has a significantly enhanced adsorption capacity for n-hexane, 70% higher than that of zeolite 5A under identical conditions. Zr-abtc (abtc4- = 3,3',5,5'-azobenzenetetracarboxylate) is capable of discriminating all three C6 alkane isomers via a thermodynamically controlled process, yielding a high separation factor for monobranched over dibranched isomers. MOFs with flexible framework may exhibit unexpected but desired adsorption properties. Ca(H2tcpb) (tcpb4- = 1,2,4,5-tetrakis(4-carboxyphenyl)-benzene) can fully separate binary or ternary mixtures of C5-C6 alkane isomers into pure form through selective molecular sieving as a result of its temperature- and adsorbate-dependent framework flexibility. The intriguing structural properties and exceptional tunability of these MOFs make them promising candidates for industrial implementation of adsorptive separation of alkane isomers. The separation of alkane isomers, particularly C5-C6 alkanes, is of paramount importance in the petrochemical industry to achieve high quality gasoline. Upon catalytic isomerization reactions, less branched alkanes (with lower octane number) need to be separated from their more branched isomers (with higher octane number) in order to improve the octane rating of gasoline. To reduce the high energy input associated with distillations, the primary separation technique currently used in industry, adsorptive separation by porous solids has been proposed. For example, zeolite 5A has been used as the adsorbent material for adsorptive separation of linear alkanes from their branched isomers, as a supplement technology to distillations. However, due to the limited number of zeolite structures and the lack of porosity tenability in these compounds, the task has not been fully fulfilled by using zeolites. Metal-organic frameworks (MOFs), in light of their structural diversity and high tunability in terms of surface area, pore size, and pore shape, offer new opportunities for resolving industrially relevant separation of alkanes through selective adsorption. This Account summarizes recent development of microporous MOFs for the separation of alkanes, with an emphasis on C5-C6 alkane isomers, including early examples of alkane separation by MOFs, as well as the latest advancement on tailor-made microporous MOFs for size sieving of C5-C6 alkane isomers. The limitation of zeolite 5A as a sorbent material for the separation of C5-C6 alkane isomers lies in its relatively low adsorption capacity. In addition, it is not capable of separating branched alkanes, which is a crucial step for further improving the octane rating of gasoline. The high porosity and tunable pore size and pore shape of MOFs may afford them higher adsorption capacity and selectivity when used for alkane separation. MOFs with pore size slightly larger than the kinetic diameter of branched alkanes can effectively separate alkane isomers through thermodynamically controlled separation, as seen in the case of Fe (bdp) (bdp = 1,4-benzenedipyrazolate). This MOF is capable of separating a mixture of hexane isomers by the degrees of branching, with higher adsorption capacity than zeolites under similar conditions but with relatively low selectivity. One effective strategy for obtaining MOFs with optimal pore size and pore shape for highly selective adsorption is to make use of reticular chemistry and precise ligand design. By applying topologically directed design strategy and precisely controlling the pore structure or ligand functionality, we have successfully synthesized a series of highly robust MOFs built on tetratopic carboxylate linkers that demonstrate high performance for the separation of C5-C6 alkane isomers. Zr-bptc (bptc = 3,3',5,5'-biphenyltetracarboxylate) adsorbs linear alkanes only and excludes all branched isomers. This size-exclusion mechanism is very similar to that of zeolite 5A. Yet, Zr-bptc has a significantly enhanced adsorption capacity for -hexane, 70% higher than that of zeolite 5A under identical conditions. Zr-abtc (abtc = 3,3',5,5'-azobenzenetetracarboxylate) is capable of discriminating all three C6 alkane isomers via a thermodynamically controlled process, yielding a high separation factor for monobranched over dibranched isomers. MOFs with flexible framework may exhibit unexpected but desired adsorption properties. Ca(H tcpb) (tcpb = 1,2,4,5-tetrakis(4-carboxyphenyl)-benzene) can fully separate binary or ternary mixtures of C5-C6 alkane isomers into pure form through selective molecular sieving as a result of its temperature- and adsorbate-dependent framework flexibility. The intriguing structural properties and exceptional tunability of these MOFs make them promising candidates for industrial implementation of adsorptive separation of alkane isomers. |
| Author | Li, Jing Wang, Hao |
| Author_xml | – sequence: 1 givenname: Hao surname: Wang fullname: Wang, Hao organization: Department of Chemistry and Chemical Biology , Rutgers University , 123 Bevier Road , Piscataway , New Jersey 08854 , United States – sequence: 2 givenname: Jing orcidid: 0000-0001-7792-4322 surname: Li fullname: Li, Jing organization: Department of Chemistry and Chemical Biology , Rutgers University , 123 Bevier Road , Piscataway , New Jersey 08854 , United States |
| BackLink | https://www.ncbi.nlm.nih.gov/pubmed/30883088$$D View this record in MEDLINE/PubMed |
| BookMark | eNpNUEtPwzAYi9AQe8A_QChHLh15NulxqhggbdqBx7X6miaorG1K0oL49wwxJA6WfbAs23M06XxnEbqkZEkJozdg4hKM8WM3xKUuCUmlPkEzKhlJhM705J-eonmMb4QQJlJ1hqacaP2DGXrZ1ib43gc_Rry1AzTJLrxCVxu8DtDaTx_2ETsf8KqKPvRD_WHxo-0hwFD7DnuHc5nkKV41e-gsfoi-tSGeo1MHTbQXR16g5_XtU36fbHZ3D_lqk4AQdEgyljoGYDOhKgaaKlkBLw1oWfKqVEJLx6o0o0wrrpxUnJVCMiVcljrOlGQLdP2b2wf_Pto4FG0djW2aQ5fDooLRTFDJFeEH69XROpatrYo-1C2Er-LvC_YNeBdkdw |
| CitedBy_id | crossref_primary_10_1016_j_chroma_2022_463493 crossref_primary_10_1021_jacs_3c04641 crossref_primary_10_1002_anie_202200947 crossref_primary_10_1002_ange_202214060 crossref_primary_10_1016_j_cej_2023_141743 crossref_primary_10_1016_j_cej_2024_151146 crossref_primary_10_1002_ange_202015257 crossref_primary_10_1002_ange_202212032 crossref_primary_10_1007_s10876_021_01993_x crossref_primary_10_1039_D3QM00430A crossref_primary_10_1002_anie_202107963 crossref_primary_10_1016_j_mtchem_2022_100840 crossref_primary_10_1002_ange_202000670 crossref_primary_10_1016_j_micromeso_2023_112970 crossref_primary_10_1002_anie_202100707 crossref_primary_10_1002_anie_202201646 crossref_primary_10_1002_anie_202219053 crossref_primary_10_1039_D0RA09307F crossref_primary_10_1016_j_micromeso_2024_113283 crossref_primary_10_1016_j_inoche_2020_108339 crossref_primary_10_1021_jacs_1c03762 crossref_primary_10_1002_smll_202412724 crossref_primary_10_1021_acsmaterialslett_4c02402 crossref_primary_10_1002_app_56009 crossref_primary_10_1016_j_cej_2023_145096 crossref_primary_10_1016_j_cjche_2020_05_023 crossref_primary_10_1002_anie_202007681 crossref_primary_10_1007_s12274_020_2714_z crossref_primary_10_1007_s10853_020_05180_7 crossref_primary_10_1016_j_memsci_2020_118426 crossref_primary_10_1016_j_jssc_2021_122541 crossref_primary_10_1021_jacs_1c12068 crossref_primary_10_1002_asia_202400899 crossref_primary_10_1016_j_cej_2024_150833 crossref_primary_10_1016_j_cej_2019_123836 crossref_primary_10_1007_s12274_020_2935_1 crossref_primary_10_3390_catal13010115 crossref_primary_10_1002_ange_202201646 crossref_primary_10_1002_anie_202017105 crossref_primary_10_1002_ange_202219053 crossref_primary_10_1016_j_enchem_2021_100057 crossref_primary_10_1038_s41467_023_35984_5 crossref_primary_10_1002_chem_202000933 crossref_primary_10_1016_j_seppur_2023_124241 crossref_primary_10_1039_D3QM00715D crossref_primary_10_1002_anie_202213959 crossref_primary_10_1002_smm2_1016 crossref_primary_10_1002_ange_202320008 crossref_primary_10_1002_aic_16236 crossref_primary_10_1016_j_micromeso_2023_112670 crossref_primary_10_1002_ange_202007681 crossref_primary_10_3724_SP_J_1123_2023_07029 crossref_primary_10_3390_molecules28114422 crossref_primary_10_1002_anie_202411960 crossref_primary_10_1016_j_seppur_2021_120010 crossref_primary_10_1002_advs_202201494 crossref_primary_10_3390_catal11020204 crossref_primary_10_1002_ange_202017105 crossref_primary_10_1016_j_apsusc_2023_157592 crossref_primary_10_1039_D0EN01011A crossref_primary_10_1007_s11426_025_2817_1 crossref_primary_10_1002_zaac_202200240 crossref_primary_10_1063_1_5120528 crossref_primary_10_1002_ange_202200947 crossref_primary_10_1016_j_fuel_2023_130006 crossref_primary_10_1016_j_seppur_2023_123203 crossref_primary_10_1021_jacs_3c02195 crossref_primary_10_1021_acs_accounts_5c00217 crossref_primary_10_1002_slct_202201863 crossref_primary_10_1002_adma_202002563 crossref_primary_10_1016_j_ccr_2025_216831 crossref_primary_10_1016_j_cej_2024_156241 crossref_primary_10_1002_adma_202002603 crossref_primary_10_1016_j_apmate_2021_12_002 crossref_primary_10_1016_j_seppur_2023_124660 crossref_primary_10_1002_ange_202308418 crossref_primary_10_1002_anie_202211359 crossref_primary_10_1016_j_chroma_2024_465357 crossref_primary_10_1002_ange_202213959 crossref_primary_10_1002_anie_202211808 crossref_primary_10_1002_anie_202015257 crossref_primary_10_1016_j_ccr_2023_215111 crossref_primary_10_1016_j_seppur_2025_132203 crossref_primary_10_1016_j_jmgm_2020_107574 crossref_primary_10_1038_s41467_024_46556_6 crossref_primary_10_1002_aic_17937 crossref_primary_10_1002_anie_202320008 crossref_primary_10_1007_s41061_019_0257_0 crossref_primary_10_1021_jacs_3c06175 crossref_primary_10_1002_ange_202411960 crossref_primary_10_1016_j_jphotochem_2023_115032 crossref_primary_10_1002_ejic_202100819 crossref_primary_10_1016_j_jssc_2021_122100 crossref_primary_10_1002_ange_202100707 crossref_primary_10_1002_anie_202308418 crossref_primary_10_1002_ange_202211808 crossref_primary_10_1016_j_jece_2023_111027 crossref_primary_10_1002_chem_202302856 crossref_primary_10_3390_separations12060152 crossref_primary_10_1039_D5SC04212G crossref_primary_10_1016_j_ccr_2020_213738 crossref_primary_10_1039_D0QI01230K crossref_primary_10_3390_chemistry3010024 crossref_primary_10_1016_j_jssc_2020_121209 crossref_primary_10_1021_jacs_0c03176 crossref_primary_10_1002_anie_202300722 crossref_primary_10_1021_jacs_3c08541 crossref_primary_10_1002_aic_70007 crossref_primary_10_1002_smll_202412312 crossref_primary_10_1002_anie_202214060 crossref_primary_10_1016_j_memsci_2022_120916 crossref_primary_10_1016_j_ccr_2024_215996 crossref_primary_10_1039_D2SC05742E crossref_primary_10_1016_j_envpol_2023_121475 crossref_primary_10_1016_j_seppur_2025_135137 crossref_primary_10_1007_s12274_020_2831_8 crossref_primary_10_1039_C9SC05721H crossref_primary_10_1016_j_seppur_2022_122095 crossref_primary_10_1002_advs_202204963 crossref_primary_10_1002_ange_202300722 crossref_primary_10_1021_jacs_4c05095 crossref_primary_10_1002_chem_202101871 crossref_primary_10_1093_nsr_nwaa094 crossref_primary_10_1002_ange_202107963 crossref_primary_10_1002_anie_202212032 crossref_primary_10_1002_anie_202000670 crossref_primary_10_1016_j_jhazmat_2022_128321 crossref_primary_10_1016_j_jiec_2022_07_047 crossref_primary_10_1039_D2SC00207H crossref_primary_10_1002_ange_202211359 |
| ContentType | Journal Article |
| DBID | NPM 7X8 |
| DOI | 10.1021/acs.accounts.8b00658 |
| DatabaseName | PubMed MEDLINE - Academic |
| DatabaseTitle | PubMed MEDLINE - Academic |
| DatabaseTitleList | MEDLINE - Academic PubMed |
| Database_xml | – sequence: 1 dbid: NPM name: PubMed url: http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed sourceTypes: Index Database – sequence: 2 dbid: 7X8 name: MEDLINE - Academic url: https://search.proquest.com/medline sourceTypes: Aggregation Database |
| DeliveryMethod | no_fulltext_linktorsrc |
| Discipline | Chemistry |
| EISSN | 1520-4898 |
| ExternalDocumentID | 30883088 |
| Genre | Research Support, U.S. Gov't, Non-P.H.S Research Support, Non-U.S. Gov't Journal Article |
| GroupedDBID | --- -DZ -~X 23M 4.4 53G 55A 5GY 5VS 5ZA 6J9 6P2 7~N 85S AABXI ABJNI ABMVS ABQRX ABUCX ACGFO ACGFS ACJ ACNCT ACS ADHLV AEESW AENEX AFEFF AFXLT AGXLV AHGAQ ALMA_UNASSIGNED_HOLDINGS AQSVZ BAANH CS3 CUPRZ D0L EBS ED~ EJD F5P GGK GNL IH2 IH9 JG~ LG6 NPM P2P RNS ROL TWZ UI2 UPT VF5 VG9 W1F WH7 XSW YIN YZZ ZCA ~02 7X8 ABBLG ABLBI |
| ID | FETCH-LOGICAL-a441t-926f2aae947d2a8175da3bca85b3db7485f2d69128737f5732b45274f96f32752 |
| IEDL.DBID | 7X8 |
| ISICitedReferencesCount | 181 |
| ISICitedReferencesURI | http://www.webofscience.com/api/gateway?GWVersion=2&SrcApp=Summon&SrcAuth=ProQuest&DestLinkType=CitingArticles&DestApp=WOS_CPL&KeyUT=000476568400022&url=https%3A%2F%2Fcvtisr.summon.serialssolutions.com%2F%23%21%2Fsearch%3Fho%3Df%26include.ft.matches%3Dt%26l%3Dnull%26q%3D |
| ISSN | 1520-4898 |
| IngestDate | Fri Jul 11 11:52:02 EDT 2025 Wed Feb 19 02:30:42 EST 2025 |
| IsPeerReviewed | true |
| IsScholarly | true |
| Issue | 7 |
| Language | English |
| LinkModel | DirectLink |
| MergedId | FETCHMERGED-LOGICAL-a441t-926f2aae947d2a8175da3bca85b3db7485f2d69128737f5732b45274f96f32752 |
| Notes | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
| ORCID | 0000-0001-7792-4322 |
| PMID | 30883088 |
| PQID | 2194153703 |
| PQPubID | 23479 |
| ParticipantIDs | proquest_miscellaneous_2194153703 pubmed_primary_30883088 |
| PublicationCentury | 2000 |
| PublicationDate | 2019-07-16 |
| PublicationDateYYYYMMDD | 2019-07-16 |
| PublicationDate_xml | – month: 07 year: 2019 text: 2019-07-16 day: 16 |
| PublicationDecade | 2010 |
| PublicationPlace | United States |
| PublicationPlace_xml | – name: United States |
| PublicationTitle | Accounts of chemical research |
| PublicationTitleAlternate | Acc Chem Res |
| PublicationYear | 2019 |
| SSID | ssj0002467 |
| Score | 2.641547 |
| Snippet | The separation of alkane isomers, particularly C5-C6 alkanes, is of paramount importance in the petrochemical industry to achieve high quality gasoline. Upon... |
| SourceID | proquest pubmed |
| SourceType | Aggregation Database Index Database |
| StartPage | 1968 |
| Title | Microporous Metal-Organic Frameworks for Adsorptive Separation of C5-C6 Alkane Isomers |
| URI | https://www.ncbi.nlm.nih.gov/pubmed/30883088 https://www.proquest.com/docview/2194153703 |
| Volume | 52 |
| WOSCitedRecordID | wos000476568400022&url=https%3A%2F%2Fcvtisr.summon.serialssolutions.com%2F%23%21%2Fsearch%3Fho%3Df%26include.ft.matches%3Dt%26l%3Dnull%26q%3D |
| hasFullText | |
| inHoldings | 1 |
| isFullTextHit | |
| isPrint | |
| link | http://cvtisr.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwpV1JSwMxFA5qBb24L3Ujgtdom2SynKQMFj20FFzorWSygCgztVP8_b7MQk-C4GFyG3hJXt73JXl5H0I3ABrCCE2JM0wS7mG7Y_rKw4RwK3iwkhlbiU3I8VhNp3rSHLiVTVplGxOrQO0KG8_I72BlAdYwcND7-ReJqlHxdrWR0FhHHQZUJqZ0yemqWjjllYIsQFSPcKVV-3SO9u-MLcHgSo-hvFVZhcS_k8wKbIa7_zVzD-00NBMPar_YR2s-P0BbaavudojeRjETD8g37PzxyAMFJ_WzTIuHbb5WiYHR4oEri8U8RkX87OtK4UWOi4DThKQCDz4_TO7xU1nEE_Aj9Dp8eEkfSaOxQAwQoSXRVARqjNdcOmoUkAmYtMwalWSx8jJXSaBOaEAxyWRIJKMZT2AnG7QIjMqEHqONvMj9KcJU9TLhgP7ZWCTMJcoJmAHbo94GbpTuout2yGbQ2XgxAfZBL2erQeuik3rcZ_O62MaMQRiM39kf_j5H28Bn4qMs0hcXqBNgBftLtGm_l-_l4qpyDmjHk9EPc1PDhQ |
| linkProvider | ProQuest |
| openUrl | ctx_ver=Z39.88-2004&ctx_enc=info%3Aofi%2Fenc%3AUTF-8&rfr_id=info%3Asid%2Fsummon.serialssolutions.com&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Ajournal&rft.genre=article&rft.atitle=Microporous+Metal-Organic+Frameworks+for+Adsorptive+Separation+of+C5-C6+Alkane+Isomers&rft.jtitle=Accounts+of+chemical+research&rft.au=Wang%2C+Hao&rft.au=Li%2C+Jing&rft.date=2019-07-16&rft.eissn=1520-4898&rft.volume=52&rft.issue=7&rft.spage=1968&rft_id=info:doi/10.1021%2Facs.accounts.8b00658&rft_id=info%3Apmid%2F30883088&rft_id=info%3Apmid%2F30883088&rft.externalDocID=30883088 |
| thumbnail_l | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/lc.gif&issn=1520-4898&client=summon |
| thumbnail_m | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/mc.gif&issn=1520-4898&client=summon |
| thumbnail_s | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/sc.gif&issn=1520-4898&client=summon |