Nucleation, Growth, and Alignment of Poly(3-hexylthiophene) Nanofibers for High-Performance OFETs
Conjugated semiconducting polymers have been the subject of intense study for over two decades with promising advances toward a printable electronics manufacturing ecosystem. These materials will deliver functional electronic devices that are lightweight, flexible, large-area, and cost-effective, wi...
Uloženo v:
| Vydáno v: | Accounts of chemical research Ročník 50; číslo 4; s. 932 |
|---|---|
| Hlavní autoři: | , , , , |
| Médium: | Journal Article |
| Jazyk: | angličtina |
| Vydáno: |
United States
18.04.2017
|
| ISSN: | 1520-4898, 1520-4898 |
| On-line přístup: | Zjistit podrobnosti o přístupu |
| Tagy: |
Přidat tag
Žádné tagy, Buďte první, kdo vytvoří štítek k tomuto záznamu!
|
| Abstract | Conjugated semiconducting polymers have been the subject of intense study for over two decades with promising advances toward a printable electronics manufacturing ecosystem. These materials will deliver functional electronic devices that are lightweight, flexible, large-area, and cost-effective, with applications ranging from biomedical sensors to solar cells. Synthesis of novel molecules has led to significant improvements in charge carrier mobility, a defining electrical performance metric for many applications. However, the solution processing and thin film deposition of conjugated polymers must also be properly controlled to obtain reproducible device performance. This has led to an abundance of research on the process-structure-property relationships governing the microstructural evolution of the model semicrystalline poly(3-hexylthiophene) (P3HT) as applied to organic field effect transistor (OFET) fabrication. What followed was the production of an expansive body of work on the crystallization, self-assembly, and charge transport behavior of this semiflexible polymer whose strong π-π stacking interactions allow for highly creative methods of structural control, including the modulation of solvent and solution properties, flow-induced crystallization and alignment techniques, structural templating, and solid-state thermal and mechanical processing. This Account relates recent progress in the microstructural control of P3HT thin films through the nucleation, growth, and alignment of P3HT nanofibers. Solution-based nanofiber formation allows one to develop structural order prior to thin film deposition, mitigating the need for intricate deposition processes and enabling the use of batch and continuous chemical processing steps. Fiber growth is framed as a traditional crystallization problem, with the balance between nucleation and growth rates determining the fiber size and ultimately the distribution of grain boundaries in the solid state. Control of nucleation can be accomplished through a sonication-based seeding procedure, while growth can be modulated through supersaturation control via the tuning of solvent quality, the use of UV irradiation or through aging. These principles carry over to the flow-induced growth of P3HT nanofibers in a continuous microfluidic processing system, leading to thin films with significantly enhanced mobility. Further gains can be made by promoting long-range polymer chain alignment, achieved by depositing nanofibers through shear-based coating methods that promote high fiber packing density and alignment. All of these developments in processing were carried out on a standard OFET platform, enabling us to generalize quantitative structure-property relationships from structural data sources such as UV-vis, AFM, and GIWAXS. It is shown that a linear correlation exists between mobility and the in-plane orientational order of nanofibers, as extracted from AFM images using advanced computer vision software developed by our group. Herein, we discuss data-driven approaches to the determination of process-structure-property relationships, as well as the transferability of structural control strategies for P3HT to other conjugated polymer systems and applications. |
|---|---|
| AbstractList | Conjugated semiconducting polymers have been the subject of intense study for over two decades with promising advances toward a printable electronics manufacturing ecosystem. These materials will deliver functional electronic devices that are lightweight, flexible, large-area, and cost-effective, with applications ranging from biomedical sensors to solar cells. Synthesis of novel molecules has led to significant improvements in charge carrier mobility, a defining electrical performance metric for many applications. However, the solution processing and thin film deposition of conjugated polymers must also be properly controlled to obtain reproducible device performance. This has led to an abundance of research on the process-structure-property relationships governing the microstructural evolution of the model semicrystalline poly(3-hexylthiophene) (P3HT) as applied to organic field effect transistor (OFET) fabrication. What followed was the production of an expansive body of work on the crystallization, self-assembly, and charge transport behavior of this semiflexible polymer whose strong π-π stacking interactions allow for highly creative methods of structural control, including the modulation of solvent and solution properties, flow-induced crystallization and alignment techniques, structural templating, and solid-state thermal and mechanical processing. This Account relates recent progress in the microstructural control of P3HT thin films through the nucleation, growth, and alignment of P3HT nanofibers. Solution-based nanofiber formation allows one to develop structural order prior to thin film deposition, mitigating the need for intricate deposition processes and enabling the use of batch and continuous chemical processing steps. Fiber growth is framed as a traditional crystallization problem, with the balance between nucleation and growth rates determining the fiber size and ultimately the distribution of grain boundaries in the solid state. Control of nucleation can be accomplished through a sonication-based seeding procedure, while growth can be modulated through supersaturation control via the tuning of solvent quality, the use of UV irradiation or through aging. These principles carry over to the flow-induced growth of P3HT nanofibers in a continuous microfluidic processing system, leading to thin films with significantly enhanced mobility. Further gains can be made by promoting long-range polymer chain alignment, achieved by depositing nanofibers through shear-based coating methods that promote high fiber packing density and alignment. All of these developments in processing were carried out on a standard OFET platform, enabling us to generalize quantitative structure-property relationships from structural data sources such as UV-vis, AFM, and GIWAXS. It is shown that a linear correlation exists between mobility and the in-plane orientational order of nanofibers, as extracted from AFM images using advanced computer vision software developed by our group. Herein, we discuss data-driven approaches to the determination of process-structure-property relationships, as well as the transferability of structural control strategies for P3HT to other conjugated polymer systems and applications.Conjugated semiconducting polymers have been the subject of intense study for over two decades with promising advances toward a printable electronics manufacturing ecosystem. These materials will deliver functional electronic devices that are lightweight, flexible, large-area, and cost-effective, with applications ranging from biomedical sensors to solar cells. Synthesis of novel molecules has led to significant improvements in charge carrier mobility, a defining electrical performance metric for many applications. However, the solution processing and thin film deposition of conjugated polymers must also be properly controlled to obtain reproducible device performance. This has led to an abundance of research on the process-structure-property relationships governing the microstructural evolution of the model semicrystalline poly(3-hexylthiophene) (P3HT) as applied to organic field effect transistor (OFET) fabrication. What followed was the production of an expansive body of work on the crystallization, self-assembly, and charge transport behavior of this semiflexible polymer whose strong π-π stacking interactions allow for highly creative methods of structural control, including the modulation of solvent and solution properties, flow-induced crystallization and alignment techniques, structural templating, and solid-state thermal and mechanical processing. This Account relates recent progress in the microstructural control of P3HT thin films through the nucleation, growth, and alignment of P3HT nanofibers. Solution-based nanofiber formation allows one to develop structural order prior to thin film deposition, mitigating the need for intricate deposition processes and enabling the use of batch and continuous chemical processing steps. Fiber growth is framed as a traditional crystallization problem, with the balance between nucleation and growth rates determining the fiber size and ultimately the distribution of grain boundaries in the solid state. Control of nucleation can be accomplished through a sonication-based seeding procedure, while growth can be modulated through supersaturation control via the tuning of solvent quality, the use of UV irradiation or through aging. These principles carry over to the flow-induced growth of P3HT nanofibers in a continuous microfluidic processing system, leading to thin films with significantly enhanced mobility. Further gains can be made by promoting long-range polymer chain alignment, achieved by depositing nanofibers through shear-based coating methods that promote high fiber packing density and alignment. All of these developments in processing were carried out on a standard OFET platform, enabling us to generalize quantitative structure-property relationships from structural data sources such as UV-vis, AFM, and GIWAXS. It is shown that a linear correlation exists between mobility and the in-plane orientational order of nanofibers, as extracted from AFM images using advanced computer vision software developed by our group. Herein, we discuss data-driven approaches to the determination of process-structure-property relationships, as well as the transferability of structural control strategies for P3HT to other conjugated polymer systems and applications. Conjugated semiconducting polymers have been the subject of intense study for over two decades with promising advances toward a printable electronics manufacturing ecosystem. These materials will deliver functional electronic devices that are lightweight, flexible, large-area, and cost-effective, with applications ranging from biomedical sensors to solar cells. Synthesis of novel molecules has led to significant improvements in charge carrier mobility, a defining electrical performance metric for many applications. However, the solution processing and thin film deposition of conjugated polymers must also be properly controlled to obtain reproducible device performance. This has led to an abundance of research on the process-structure-property relationships governing the microstructural evolution of the model semicrystalline poly(3-hexylthiophene) (P3HT) as applied to organic field effect transistor (OFET) fabrication. What followed was the production of an expansive body of work on the crystallization, self-assembly, and charge transport behavior of this semiflexible polymer whose strong π-π stacking interactions allow for highly creative methods of structural control, including the modulation of solvent and solution properties, flow-induced crystallization and alignment techniques, structural templating, and solid-state thermal and mechanical processing. This Account relates recent progress in the microstructural control of P3HT thin films through the nucleation, growth, and alignment of P3HT nanofibers. Solution-based nanofiber formation allows one to develop structural order prior to thin film deposition, mitigating the need for intricate deposition processes and enabling the use of batch and continuous chemical processing steps. Fiber growth is framed as a traditional crystallization problem, with the balance between nucleation and growth rates determining the fiber size and ultimately the distribution of grain boundaries in the solid state. Control of nucleation can be accomplished through a sonication-based seeding procedure, while growth can be modulated through supersaturation control via the tuning of solvent quality, the use of UV irradiation or through aging. These principles carry over to the flow-induced growth of P3HT nanofibers in a continuous microfluidic processing system, leading to thin films with significantly enhanced mobility. Further gains can be made by promoting long-range polymer chain alignment, achieved by depositing nanofibers through shear-based coating methods that promote high fiber packing density and alignment. All of these developments in processing were carried out on a standard OFET platform, enabling us to generalize quantitative structure-property relationships from structural data sources such as UV-vis, AFM, and GIWAXS. It is shown that a linear correlation exists between mobility and the in-plane orientational order of nanofibers, as extracted from AFM images using advanced computer vision software developed by our group. Herein, we discuss data-driven approaches to the determination of process-structure-property relationships, as well as the transferability of structural control strategies for P3HT to other conjugated polymer systems and applications. |
| Author | McBride, Michael Persson, Nils E Chu, Ping-Hsun Grover, Martha Reichmanis, Elsa |
| Author_xml | – sequence: 1 givenname: Nils E surname: Persson fullname: Persson, Nils E organization: School of Chemical & Biomolecular Engineering, ‡School of Chemistry & Biochemistry, and §School of Materials Science & Engineering, Georgia Institute of Technology , Atlanta, Georgia 30332, United States – sequence: 2 givenname: Ping-Hsun surname: Chu fullname: Chu, Ping-Hsun organization: School of Chemical & Biomolecular Engineering, ‡School of Chemistry & Biochemistry, and §School of Materials Science & Engineering, Georgia Institute of Technology , Atlanta, Georgia 30332, United States – sequence: 3 givenname: Michael surname: McBride fullname: McBride, Michael organization: School of Chemical & Biomolecular Engineering, ‡School of Chemistry & Biochemistry, and §School of Materials Science & Engineering, Georgia Institute of Technology , Atlanta, Georgia 30332, United States – sequence: 4 givenname: Martha surname: Grover fullname: Grover, Martha organization: School of Chemical & Biomolecular Engineering, ‡School of Chemistry & Biochemistry, and §School of Materials Science & Engineering, Georgia Institute of Technology , Atlanta, Georgia 30332, United States – sequence: 5 givenname: Elsa orcidid: 0000-0002-8205-8016 surname: Reichmanis fullname: Reichmanis, Elsa organization: School of Chemical & Biomolecular Engineering, ‡School of Chemistry & Biochemistry, and §School of Materials Science & Engineering, Georgia Institute of Technology , Atlanta, Georgia 30332, United States |
| BackLink | https://www.ncbi.nlm.nih.gov/pubmed/28234458$$D View this record in MEDLINE/PubMed |
| BookMark | eNpNkE1Lw0AYhBep2A_9ByJ7rNDUzZvdZHMsRVuhtD3oOWw2b5pIsluzCZp_b8AKnuZhZpjDTMnIWIOE3Pts6TPwn5R2S6W17UzrlmHKWBjEV2TiC2Ael7Ec_eMxmTr3wRgDHkY3ZAwSAs6FnBC173SFqi2tWdBNY7_aYkGVyeiqKk-mRtNSm9Ojrfp54BX43VdtUdpzgQYf6V4Zm5cpNo7mtqHb8lR4R2wGrpXRSA8vz2_ullznqnJ4d9EZeR_s9dbbHTav69XOU9znradjybNcB3kkOXAMuEQOEEnGldChEjKNNROaBUOSZmGOvszCNGMAmeAQIszI_Hf33NjPDl2b1KXTWFXKoO1c4ssIRBRDLIbqw6XapTVmybkpa9X0yd8t8AMem2h1 |
| CitedBy_id | crossref_primary_10_1246_cl_200597 crossref_primary_10_1039_D0QM00980F crossref_primary_10_3390_polym14194125 crossref_primary_10_3390_pr6070079 crossref_primary_10_1038_s41563_019_0340_5 crossref_primary_10_1002_admt_201800554 crossref_primary_10_1038_s41428_018_0062_6 crossref_primary_10_1021_acsmacrolett_5c00525 crossref_primary_10_1039_C9NR01491H crossref_primary_10_1002_adfm_202409982 crossref_primary_10_1021_acs_macromol_5c01262 crossref_primary_10_1073_pnas_2000398117 crossref_primary_10_1002_smll_202105306 crossref_primary_10_1002_anie_202216049 crossref_primary_10_1002_cjoc_202100355 crossref_primary_10_1016_j_polymer_2018_04_052 crossref_primary_10_1002_admi_201700875 crossref_primary_10_1016_j_polymer_2020_122959 crossref_primary_10_1016_j_orgel_2017_09_038 crossref_primary_10_1016_j_polymer_2024_126719 crossref_primary_10_6023_A21030086 crossref_primary_10_1016_j_polymer_2018_07_062 crossref_primary_10_1002_ange_202315740 crossref_primary_10_1016_j_apsusc_2024_161673 crossref_primary_10_1002_polb_24796 crossref_primary_10_1002_smll_202400874 crossref_primary_10_1038_s41467_019_10519_z crossref_primary_10_1002_marc_202200529 crossref_primary_10_1016_j_orgel_2018_07_023 crossref_primary_10_1039_D5MA00326A crossref_primary_10_1088_2051_672X_ac7b3b crossref_primary_10_1039_C8PY01529E crossref_primary_10_1002_anie_201911311 crossref_primary_10_1016_j_ijbiomac_2023_127232 crossref_primary_10_1002_adma_202007041 crossref_primary_10_1070_RCR4973 crossref_primary_10_1155_2024_6649421 crossref_primary_10_1016_j_eurpolymj_2022_111032 crossref_primary_10_1016_j_mattod_2020_08_017 crossref_primary_10_1002_adma_201705052 crossref_primary_10_1038_s41578_020_00233_4 crossref_primary_10_1016_j_progpolymsci_2019_101179 crossref_primary_10_1039_D0SC00806K crossref_primary_10_1002_chem_201804457 crossref_primary_10_1002_anie_202315740 crossref_primary_10_1002_adfm_202105456 crossref_primary_10_1002_pol_20240377 crossref_primary_10_1016_j_polymer_2022_125178 crossref_primary_10_1088_1361_6528_aa9d7c crossref_primary_10_1039_C9NH00694J crossref_primary_10_1039_D0MH02047H crossref_primary_10_1002_chem_202002559 crossref_primary_10_1016_j_chroma_2018_07_047 crossref_primary_10_1016_j_progpolymsci_2020_101279 crossref_primary_10_1002_adma_202309679 crossref_primary_10_1016_j_nanoen_2022_107489 crossref_primary_10_1021_jacs_7b13701 crossref_primary_10_1016_j_orgel_2018_03_033 crossref_primary_10_1002_adma_201806863 crossref_primary_10_1002_ange_201911311 crossref_primary_10_1002_bte2_20220013 crossref_primary_10_1016_j_orgel_2017_12_030 crossref_primary_10_1002_adfm_202107925 crossref_primary_10_1002_macp_202200151 crossref_primary_10_1016_j_adna_2025_05_001 crossref_primary_10_1002_pol_20240148 crossref_primary_10_1002_ange_202216049 crossref_primary_10_1016_j_heliyon_2022_e10206 crossref_primary_10_1039_D5MH00096C crossref_primary_10_3390_polym12051188 crossref_primary_10_1007_s10118_023_3042_z crossref_primary_10_1002_adfm_202312223 crossref_primary_10_3390_app10196886 crossref_primary_10_1007_s11664_020_08242_3 crossref_primary_10_1016_j_jpowsour_2017_11_062 crossref_primary_10_1021_jacs_2c04984 |
| ContentType | Journal Article |
| DBID | NPM 7X8 |
| DOI | 10.1021/acs.accounts.6b00639 |
| DatabaseName | PubMed MEDLINE - Academic |
| DatabaseTitle | PubMed MEDLINE - Academic |
| DatabaseTitleList | MEDLINE - Academic PubMed |
| Database_xml | – sequence: 1 dbid: NPM name: PubMed url: http://www.ncbi.nlm.nih.gov/entrez/query.fcgi?db=PubMed sourceTypes: Index Database – sequence: 2 dbid: 7X8 name: MEDLINE - Academic url: https://search.proquest.com/medline sourceTypes: Aggregation Database |
| DeliveryMethod | no_fulltext_linktorsrc |
| Discipline | Chemistry |
| EISSN | 1520-4898 |
| ExternalDocumentID | 28234458 |
| Genre | Research Support, U.S. Gov't, Non-P.H.S Journal Article |
| GroupedDBID | --- -DZ -~X 23M 4.4 53G 55A 5GY 5VS 5ZA 6J9 6P2 7~N 85S AABXI ABBLG ABJNI ABLBI ABMVS ABQRX ABUCX ACGFO ACGFS ACJ ACNCT ACS ADHLV AEESW AENEX AETEA AFEFF AFXLT AGXLV AHGAQ ALMA_UNASSIGNED_HOLDINGS AQSVZ BAANH CS3 CUPRZ D0L EBS ED~ EJD F5P GGK GNL IH2 IH9 JG~ LG6 NPM P2P RNS ROL TWZ UI2 UPT VF5 VG9 W1F WH7 XSW YZZ ZCA ~02 7X8 |
| ID | FETCH-LOGICAL-a414t-c984dfc3f78424e348e4227804a5c6a58b9c05c03348bd6fe18d6bd022d5426e2 |
| IEDL.DBID | 7X8 |
| ISICitedReferencesCount | 138 |
| ISICitedReferencesURI | http://www.webofscience.com/api/gateway?GWVersion=2&SrcApp=Summon&SrcAuth=ProQuest&DestLinkType=CitingArticles&DestApp=WOS_CPL&KeyUT=000399859800030&url=https%3A%2F%2Fcvtisr.summon.serialssolutions.com%2F%23%21%2Fsearch%3Fho%3Df%26include.ft.matches%3Dt%26l%3Dnull%26q%3D |
| ISSN | 1520-4898 |
| IngestDate | Thu Oct 02 05:03:09 EDT 2025 Mon Jul 21 06:05:32 EDT 2025 |
| IsPeerReviewed | true |
| IsScholarly | true |
| Issue | 4 |
| Language | English |
| LinkModel | DirectLink |
| MergedId | FETCHMERGED-LOGICAL-a414t-c984dfc3f78424e348e4227804a5c6a58b9c05c03348bd6fe18d6bd022d5426e2 |
| Notes | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
| ORCID | 0000-0002-8205-8016 |
| PMID | 28234458 |
| PQID | 1872579295 |
| PQPubID | 23479 |
| ParticipantIDs | proquest_miscellaneous_1872579295 pubmed_primary_28234458 |
| PublicationCentury | 2000 |
| PublicationDate | 2017-04-18 |
| PublicationDateYYYYMMDD | 2017-04-18 |
| PublicationDate_xml | – month: 04 year: 2017 text: 2017-04-18 day: 18 |
| PublicationDecade | 2010 |
| PublicationPlace | United States |
| PublicationPlace_xml | – name: United States |
| PublicationTitle | Accounts of chemical research |
| PublicationTitleAlternate | Acc Chem Res |
| PublicationYear | 2017 |
| SSID | ssj0002467 |
| Score | 2.573109 |
| Snippet | Conjugated semiconducting polymers have been the subject of intense study for over two decades with promising advances toward a printable electronics... |
| SourceID | proquest pubmed |
| SourceType | Aggregation Database Index Database |
| StartPage | 932 |
| Title | Nucleation, Growth, and Alignment of Poly(3-hexylthiophene) Nanofibers for High-Performance OFETs |
| URI | https://www.ncbi.nlm.nih.gov/pubmed/28234458 https://www.proquest.com/docview/1872579295 |
| Volume | 50 |
| WOSCitedRecordID | wos000399859800030&url=https%3A%2F%2Fcvtisr.summon.serialssolutions.com%2F%23%21%2Fsearch%3Fho%3Df%26include.ft.matches%3Dt%26l%3Dnull%26q%3D |
| hasFullText | |
| inHoldings | 1 |
| isFullTextHit | |
| isPrint | |
| link | http://cvtisr.summon.serialssolutions.com/2.0.0/link/0/eLvHCXMwpV1LS8NAEF7UCnrx_agvVvCg0LV57Kabk5Ri9WLMQaG3sq_YQkmqqWL_vbPbhJ4EwUtyStjsTOb7dndmPoSudAywzYwkArCGUK0l4ZwGxFAjhVJSKk84sYlOkvDBIE6rDbeySqusY6IL1LpQdo-87fMOeBeAObubvhOrGmVPVysJjVXUCIHK2JSuzmDZLTygTkEWIMojlMe8Lp0L_LZQJQzY6TGUt5F0SP07yXRg09_-7zB30FZFM3F34Re7aMXke2ijV6u77SOR2EbGziwt_ABr8dmohUWucXcyfnMZArjIcFpM5tchGZnv-WQ2GtseBLm5wRCSwSclMEcMnBfbXBGSLisQ8HP__qU8QK9w6z2SSm6BCOrTGVExpzpTYdYBY1ETUm6oLZT1qGAqEozLWHlMebZ2V-ooMz7XkdRAAjQDnDfBIVrLi9wcI2yyULAYyIZk8CbgoBA6Mma4hAVTGEvVRJf17A3hu-0ZhchN8VkOl_PXREcLEwyni74bQ1gdhpQyfvKHp0_RZmAB2HZl5GeokcHPbM7RuvqajcuPC-cncE3Spx_a-cjr |
| linkProvider | ProQuest |
| openUrl | ctx_ver=Z39.88-2004&ctx_enc=info%3Aofi%2Fenc%3AUTF-8&rfr_id=info%3Asid%2Fsummon.serialssolutions.com&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Ajournal&rft.genre=article&rft.atitle=Nucleation%2C+Growth%2C+and+Alignment+of+Poly%283-hexylthiophene%29+Nanofibers+for+High-Performance+OFETs&rft.jtitle=Accounts+of+chemical+research&rft.au=Persson%2C+Nils+E&rft.au=Chu%2C+Ping-Hsun&rft.au=McBride%2C+Michael&rft.au=Grover%2C+Martha&rft.date=2017-04-18&rft.eissn=1520-4898&rft.volume=50&rft.issue=4&rft.spage=932&rft_id=info:doi/10.1021%2Facs.accounts.6b00639&rft_id=info%3Apmid%2F28234458&rft_id=info%3Apmid%2F28234458&rft.externalDocID=28234458 |
| thumbnail_l | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/lc.gif&issn=1520-4898&client=summon |
| thumbnail_m | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/mc.gif&issn=1520-4898&client=summon |
| thumbnail_s | http://covers-cdn.summon.serialssolutions.com/index.aspx?isbn=/sc.gif&issn=1520-4898&client=summon |