Structural Ordering and Charge Variation Induced by Cation Substitution in (Sr,Ca)AlSiN3:Eu Phosphor
Nitride phosphors are suitable for white light-emitting diode applications. In this study, the structure of phosphor has been modified through cation substitution to induce charge variation and a rearrangement of neighboring nitride clusters, and consequently enhance its luminescent behavior. Substi...
Uložené v:
| Vydané v: | Journal of the American Chemical Society Ročník 137; číslo 28; s. 8936 - 8939 |
|---|---|
| Hlavní autori: | , , , , , |
| Médium: | Journal Article |
| Jazyk: | English |
| Vydavateľské údaje: |
United States
22.07.2015
|
| ISSN: | 1520-5126 |
| On-line prístup: | Zistit podrobnosti o prístupe |
| Tagy: |
Pridať tag
Žiadne tagy, Buďte prvý, kto otaguje tento záznam!
|
| Shrnutí: | Nitride phosphors are suitable for white light-emitting diode applications. In this study, the structure of phosphor has been modified through cation substitution to induce charge variation and a rearrangement of neighboring nitride clusters, and consequently enhance its luminescent behavior. Substitution of Ca(2+) by Sr(2+) cations expanded the lattice volume and the bc plane, but shortened the distance between the layers along the a axis. Lattice distortion of the framework introduced high-coordination sites in the Sr/Eu centers and adequate space, thereby facilitating charge variation of activators under reduced atmosphere, as detected through X-ray absorption near-edge structure spectroscopy. As such, the photoluminescent intensity of the phosphors increased by more than 10% and a blue shift occurred. The microstructures of the samples were also analyzed using high-resolution transmission electron microscopy. Cation substitution induced a special change in the anion environment, as indicated in the solid-state Raman spectra. Moreover, typical ordering variations in the SiN4 and AlN4 clusters are generated in the lattice. Meanwhile, neighbor sequence of (Si/Al)N4 around the divalent centers were observed through solid-state nuclear magnetic resonance spectroscopy. The modified ordering distribution resulted in a rigid structure and improved the thermal quenching behavior. Thermal stability has been enhanced by 10% at 473 K when x = 0.9 in SrxCa0.993-xAlSiN3:Eu(2+)0.007 compared with that at x = 0. This study promotes the research of neighbor sequence for selective tetrahedral sites such as Li, Mg, Al, and Si coordinated by N atoms in contact with cation sites. |
|---|---|
| Bibliografia: | ObjectType-Article-1 SourceType-Scholarly Journals-1 ObjectType-Feature-2 content type line 23 |
| ISSN: | 1520-5126 |
| DOI: | 10.1021/jacs.5b06080 |