Модификация поверхностного слоя композиционных мембран
Uloženo v:
| Název: | Модификация поверхностного слоя композиционных мембран |
|---|---|
| Autoři: | Fazullin, D.D., Mavrin, G.V., Fazullina, L.I. |
| Zdroj: | Электронная обработка материалов (2) 11-17 |
| Informace o vydavateli: | 2025. |
| Rok vydání: | 2025 |
| Témata: | porosity, краевой угол смачивания, ацетонитрил, IRFourier spectroscopy, celluloseacetate, Acetone, acetonitrile, композиционные мембраны, пористость, ацетат целлюлозы, ethanol, composite membranes, contact angle, этанол, ИК-Фурье-спектроскопия, ацетон |
| Popis: | The work contains studies on increasing the porosity of the surface layer of composite membranes. In order to increase the porosity of composite membranes, solvents such as ethanol and acetonitrile, the boiling point of which is higher than that of acetone, which was used as the main cellulose acetate, were added to the polymer solution as a porogen. Based on the results of the study, samples of composite membranes were obtained and their physicochemical properties such as total porosity, layer thickness, water absorption, and wetting angle were studied, and IR spectra of the membranes were obtained. The specific productivity and retention capacity of the obtained microfiltration membranes were also established. Проведены исследования по повышению пористости поверхностного слоя композиционных мембран. Для этого в состав раствора полимера в качестве порообразователя добавлены такие растворители, как этанол и ацетонитрил, температура кипения которых выше, чем у ацетона, использованного как основной ацетат целлюлозы. По результатам исследования получены образцы композиционных мембран и изучены физико-химические свойства, такие как общая пористость, толщина слоя, водопоглощение, краевой угол смачивания, а также ИК-спектры мембран. Установлены удельная производительность и задерживающая способность полученных микрофильтрационных мембран. |
| Druh dokumentu: | Article |
| Popis souboru: | application/pdf |
| Jazyk: | Russian |
| Přístupová URL adresa: | https://ibn.idsi.md/vizualizare_articol/227919 |
| Přístupové číslo: | edsair.od......4168..f9a8a9b3d22af29b232e4f152be3544f |
| Databáze: | OpenAIRE |
Nájsť tento článok vo Web of Science | Abstrakt: | The work contains studies on increasing the porosity of the surface layer of composite membranes. In order to increase the porosity of composite membranes, solvents such as ethanol and acetonitrile, the boiling point of which is higher than that of acetone, which was used as the main cellulose acetate, were added to the polymer solution as a porogen. Based on the results of the study, samples of composite membranes were obtained and their physicochemical properties such as total porosity, layer thickness, water absorption, and wetting angle were studied, and IR spectra of the membranes were obtained. The specific productivity and retention capacity of the obtained microfiltration membranes were also established.<br />Проведены исследования по повышению пористости поверхностного слоя композиционных мембран. Для этого в состав раствора полимера в качестве порообразователя добавлены такие растворители, как этанол и ацетонитрил, температура кипения которых выше, чем у ацетона, использованного как основной ацетат целлюлозы. По результатам исследования получены образцы композиционных мембран и изучены физико-химические свойства, такие как общая пористость, толщина слоя, водопоглощение, краевой угол смачивания, а также ИК-спектры мембран. Установлены удельная производительность и задерживающая способность полученных микрофильтрационных мембран. |
|---|