Третичная альфа-фаза в сплавах титана
Uloženo v:
| Název: | Третичная альфа-фаза в сплавах титана |
|---|---|
| Autoři: | Kutsebina, Еlena Y., Kalienko, Maksim S., Volkov, Anatoly V. |
| Informace o vydavateli: | Издательский дом «Ажур», 2024. |
| Rok vydání: | 2024 |
| Témata: | TERTIARY Α-PHASE, МИКРОСТРУКТУРА, ТРЕТИЧНАЯ Α-ФАЗА, VT9 TITANIUM ALLOY, СКОРОСТЬ ОХЛАЖДЕНИЯ, ТИТАНОВЫЙ СПЛАВ ВТ9, ДИФФЕРЕНЦИАЛЬНАЯ СКАНИРУЮЩАЯ КАЛОРИМЕТРИЯ, MICROSTRUCTURE, COOLING RATE, DIFFERENTIAL SCANNING CALORIMETRY |
| Popis: | The work investigated the influence of heat treatment modes on the microstructure of titanium alloy VT9. The microstructure of the alloy in the initial state after high-temperature treatment in the (α+β) region and aging is represented by the α-phase of three morphologies (globular primary, lamellar secondary, finely dispersed tertiary) and the β-phase. It has been established that when varying the cooling rate in air after high-temperature treatment, the formation of a fine tertiary α-phase is observed in all cases. It has been shown that the dissolution of the tertiary α-phase occurs above 700 °C, but in this case titanium silicide particles are formed. В работе исследовано влияние режимов термической обработки на микроструктуру титанового сплава ВТ9. Микроструктура сплава в исходном состоянии после высокотемпературной обработки в (α+β)-области и старения представлена α-фазой трех морфологий (глобулярная первичная, пластинчатая вторичная, мелкодисперсная третичная) и β-фазой. Установлено, что при варьировании скорости охлаждения на воздухе после высокотемпературной обработки во всех случаях наблюдается образование мелкодисперсной третичной α-фазы. Показано, что растворение третичной α-фазы происходит выше 700 °С, но при этом образуются частицы силицидов титана. |
| Druh dokumentu: | Conference object |
| Popis souboru: | application/pdf |
| Jazyk: | Russian |
| Přístupová URL adresa: | http://elar.urfu.ru/handle/10995/128897 |
| Přístupové číslo: | edsair.od.......917..98f9c803fd88a57dba6a43483970c260 |
| Databáze: | OpenAIRE |
Nájsť tento článok vo Web of Science | Abstrakt: | The work investigated the influence of heat treatment modes on the microstructure of titanium alloy VT9. The microstructure of the alloy in the initial state after high-temperature treatment in the (α+β) region and aging is represented by the α-phase of three morphologies (globular primary, lamellar secondary, finely dispersed tertiary) and the β-phase. It has been established that when varying the cooling rate in air after high-temperature treatment, the formation of a fine tertiary α-phase is observed in all cases. It has been shown that the dissolution of the tertiary α-phase occurs above 700 °C, but in this case titanium silicide particles are formed.<br />В работе исследовано влияние режимов термической обработки на микроструктуру титанового сплава ВТ9. Микроструктура сплава в исходном состоянии после высокотемпературной обработки в (α+β)-области и старения представлена α-фазой трех морфологий (глобулярная первичная, пластинчатая вторичная, мелкодисперсная третичная) и β-фазой. Установлено, что при варьировании скорости охлаждения на воздухе после высокотемпературной обработки во всех случаях наблюдается образование мелкодисперсной третичной α-фазы. Показано, что растворение третичной α-фазы происходит выше 700 °С, но при этом образуются частицы силицидов титана. |
|---|